Mechanical Fracture Parameters of Extruded Polystyrene

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F18%3APU128707" target="_blank" >RIV/00216305:26110/18:PU128707 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.776.160" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.776.160</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.776.160" target="_blank" >10.4028/www.scientific.net/KEM.776.160</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical Fracture Parameters of Extruded Polystyrene

Popis výsledku v původním jazyce

Extruded polystyrene (XPS) is a material with applications in the building industry, where it is typically used as thermal insulation. Fracture experiments in the three-point bending configuration were conducted on XPS beam specimens with an initial stress concentrator made before testing. The nominal dimensions of the beams were 40 x 40 x 160 mm. The depth of the initial edge notch on the bottom side of the specimen was approximately 1/3 of specimen height. The span length was 120 mm. Load vs. displacement diagrams were recorded during fracture tests, and subsequently the modulus of elasticity (E), effective fracture toughness (KIce) and specific fracture energy (GF) of the XPS were determined.

Název v anglickém jazyce

Mechanical Fracture Parameters of Extruded Polystyrene

Popis výsledku anglicky

Extruded polystyrene (XPS) is a material with applications in the building industry, where it is typically used as thermal insulation. Fracture experiments in the three-point bending configuration were conducted on XPS beam specimens with an initial stress concentrator made before testing. The nominal dimensions of the beams were 40 x 40 x 160 mm. The depth of the initial edge notch on the bottom side of the specimen was approximately 1/3 of specimen height. The span length was 120 mm. Load vs. displacement diagrams were recorded during fracture tests, and subsequently the modulus of elasticity (E), effective fracture toughness (KIce) and specific fracture energy (GF) of the XPS were determined.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GA16-18702S" target="_blank" >GA16-18702S: Problematika porušování v blízkosti rozhraní plniva a matrice kompozitů na silikátové bázi (AMIRI)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Key Engineering Materials: Rehabilitation and Reconstruction of Buildings

ISBN

978-3-0357-1361-9

ISSN

1013-9826

e-ISSN

—

Počet stran výsledku

4

Strana od-do

160-163

Název nakladatele

Trans Tech Publications

Místo vydání

Switzerland

Místo konání akce

Praha

Datum konání akce

23. 11. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—