Study on the differences between surface fracture areas for different sizes of modCT specimens
Popis výsledku v původním jazyce
The study of the different types of surface roughness – depending on the three different sizes used during destructive loading experiments is the main topic of this paper. The specimens were subjected to modified compact tension tests (modCT). Concrete material was used so the quasi-brittle fracture is represented. Change of roughness (through fracture surface area) is in-vestigated by 2D laser profilometer scanning.
Název v anglickém jazyce
Study on the differences between surface fracture areas for different sizes of modCT specimens
Popis výsledku anglicky
The study of the different types of surface roughness – depending on the three different sizes used during destructive loading experiments is the main topic of this paper. The specimens were subjected to modified compact tension tests (modCT). Concrete material was used so the quasi-brittle fracture is represented. Change of roughness (through fracture surface area) is in-vestigated by 2D laser profilometer scanning.

Projekt
<a href="/cs/project/GJ18-12289Y" target="_blank" >GJ18-12289Y: Pokročilý popis šíření trhlin v kompozitech na bázi alkalicky aktivované matrice</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)