Influence of the Interfacial Transition Zone on crack behavior in a matrix/aggregate system
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F18%3APU131824" target="_blank" >RIV/00216305:26110/18:PU131824 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/18:00498923
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.prostr.2018.12.357" target="_blank" >http://dx.doi.org/10.1016/j.prostr.2018.12.357</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.prostr.2018.12.357" target="_blank" >10.1016/j.prostr.2018.12.357</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of the Interfacial Transition Zone on crack behavior in a matrix/aggregate system
Popis výsledku v původním jazyce
Fracture behavior of a crack in a matrix/aggregate (MTX/AGG) system is studied. Influence of the Interfacial Transition Zone (ITZ) between the individual phases on the fracture response is investigated. It is discussed how the crack propagation process depends on properties of matrix and aggregate but especially the influence of the ITZ (that arises between the individual layers) is investigated. Various combinations of materials of matrix, aggregate and ITZ affect the fracture behavior of the whole system. Numerical simulations of a crack terminating at the MTX/ITZ interface based on the finite element method are presented to analyze the critical loading and discuss the effects of several parameters (ITZ thickness, AGG radius, MTX/ITZ elastic mismatch) on the crack propagation near a bi-material interface.
Název v anglickém jazyce
Influence of the Interfacial Transition Zone on crack behavior in a matrix/aggregate system
Popis výsledku anglicky
Fracture behavior of a crack in a matrix/aggregate (MTX/AGG) system is studied. Influence of the Interfacial Transition Zone (ITZ) between the individual phases on the fracture response is investigated. It is discussed how the crack propagation process depends on properties of matrix and aggregate but especially the influence of the ITZ (that arises between the individual layers) is investigated. Various combinations of materials of matrix, aggregate and ITZ affect the fracture behavior of the whole system. Numerical simulations of a crack terminating at the MTX/ITZ interface based on the finite element method are presented to analyze the critical loading and discuss the effects of several parameters (ITZ thickness, AGG radius, MTX/ITZ elastic mismatch) on the crack propagation near a bi-material interface.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20101 - Civil engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GA16-18702S" target="_blank" >GA16-18702S: Problematika porušování v blízkosti rozhraní plniva a matrice kompozitů na silikátové bázi (AMIRI)</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
22th European Conference on Fracture
ISBN
—
ISSN
2452-3216
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1798-1803
Název nakladatele
Neuveden
Místo vydání
Bělehrad, Srbsko
Místo konání akce
Beograd
Datum konání akce
26. 8. 2018
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
000459860900297