Influence of Class C Fly Ash on the Properties of Plastic Clay and Fired Brick Body

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F20%3APU135559" target="_blank" >RIV/00216305:26110/20:PU135559 - isvavai.cz</a>

Výsledek na webu

<a href="http://mit.imt.si/izvodi/mit201/sokolar.pdf" target="_blank" >http://mit.imt.si/izvodi/mit201/sokolar.pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.17222/mit.2019.148" target="_blank" >10.17222/mit.2019.148</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Class C Fly Ash on the Properties of Plastic Clay and Fired Brick Body

Popis výsledku v původním jazyce

Class C fly ash (CCFA) was used, according to ASTM C618-12a, as an admixture (10 %/w) in calcareous brick clay to determine the difference (in comparison with pure clay) in the clay body plasticity (CCFA increases the water content, decreases the drying shrinkage, drying sensitivity and bulk density of a green body) and in the properties of a fired body (since CCFA acts as a pore-forming agent, we can expect a lower bulk density and better thermal insulation). Due to low firing temperatures of the brick body (850 °C and 1000 °C), there is no risk of an anhydrite decomposition as Class C fly ash does not increase the SO2 content in flue gas during the firing and efflorescence.

Název v anglickém jazyce

Influence of Class C Fly Ash on the Properties of Plastic Clay and Fired Brick Body

Popis výsledku anglicky

Class C fly ash (CCFA) was used, according to ASTM C618-12a, as an admixture (10 %/w) in calcareous brick clay to determine the difference (in comparison with pure clay) in the clay body plasticity (CCFA increases the water content, decreases the drying shrinkage, drying sensitivity and bulk density of a green body) and in the properties of a fired body (since CCFA acts as a pore-forming agent, we can expect a lower bulk density and better thermal insulation). Due to low firing temperatures of the brick body (850 °C and 1000 °C), there is no risk of an anhydrite decomposition as Class C fly ash does not increase the SO2 content in flue gas during the firing and efflorescence.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA18-02815S" target="_blank" >GA18-02815S: Eliminace emisí oxidu siřičitého při výpalu keramického střepu na bázi fluidních elektrárenských popílků</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiali in tehnologije

ISSN

1580-2949

e-ISSN

1580-3414

Svazek periodika

54

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

5

Strana od-do

107-111

Kód UT WoS článku

000536656900015

EID výsledku v databázi Scopus

2-s2.0-85081674417