Mechanical fracture characterization of alkali-activated slag mortars with standardized and natural sand
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F20%3APU135873" target="_blank" >RIV/00216305:26110/20:PU135873 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.matec-conferences.org/articles/matecconf/abs/2020/06/matecconf_space20_00021/matecconf_space20_00021.html" target="_blank" >https://www.matec-conferences.org/articles/matecconf/abs/2020/06/matecconf_space20_00021/matecconf_space20_00021.html</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1051/matecconf/202031000021" target="_blank" >10.1051/matecconf/202031000021</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical fracture characterization of alkali-activated slag mortars with standardized and natural sand
Popis výsledku v původním jazyce
This paper is focused on the development of the physical, mechanical and fracture characteristics of alkali-activated slag (AAS) mortars during ageing. The two AAS mortars were selected for the purpose of the experiment. The difference was in a type of used sand: first mortar was made using the standardized siliceous sand with the maximum nominal grain size of 2 mm and the second mortar using the natural sand with a maximum grain size of 4 mm. The results of the elastic, fracture and strength parameters determined within the time interval of 3 to 330 days of ageing are summarized in the paper. All experimental results were evaluated for the prismatic specimens with dimensions of 40 × 40 × 160 mm and were expressed by the average value and sample standard deviation calculated from three independent measurements
Název v anglickém jazyce
Mechanical fracture characterization of alkali-activated slag mortars with standardized and natural sand
Popis výsledku anglicky
This paper is focused on the development of the physical, mechanical and fracture characteristics of alkali-activated slag (AAS) mortars during ageing. The two AAS mortars were selected for the purpose of the experiment. The difference was in a type of used sand: first mortar was made using the standardized siliceous sand with the maximum nominal grain size of 2 mm and the second mortar using the natural sand with a maximum grain size of 4 mm. The results of the elastic, fracture and strength parameters determined within the time interval of 3 to 330 days of ageing are summarized in the paper. All experimental results were evaluated for the prismatic specimens with dimensions of 40 × 40 × 160 mm and were expressed by the average value and sample standard deviation calculated from three independent measurements
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20101 - Civil engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GJ18-12289Y" target="_blank" >GJ18-12289Y: Pokročilý popis šíření trhlin v kompozitech na bázi alkalicky aktivované matrice</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
SPACE 2019
ISBN
978-80-553-3413-4
ISSN
2261-236X
e-ISSN
—
Počet stran výsledku
9
Strana od-do
1-9
Název nakladatele
EDP Sciences
Místo vydání
France
Místo konání akce
Štrbské Pleso
Datum konání akce
13. 11. 2019
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
000638061500021