Fatigue life of S960 high strength steel with laser cladded functional surface layers
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F24%3APU154913" target="_blank" >RIV/00216305:26110/24:PU154913 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/24:00587941
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S1350630724006757?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1350630724006757?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.engfailanal.2024.108629" target="_blank" >10.1016/j.engfailanal.2024.108629</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue life of S960 high strength steel with laser cladded functional surface layers
Popis výsledku v původním jazyce
This study evaluates the fatigue life of S960 high-strength steel with laser-cladded layers of aluminium bronze, hard chrome, cobalt alloy, and stainless steel, using three-point bending tests. Our results demonstrate that while these cladded layers offer potential for enhanced surface properties, they generally reduce the material's fatigue life due to alterations in the heat-affected zone and the introduction of microstructural defects at layer interfaces. The extent of fatigue life reduction varies with the type of cladded layer, highlighting the importance of optimizing laser cladding parameters to minimize detrimental effects and improve component longevity.
Název v anglickém jazyce
Fatigue life of S960 high strength steel with laser cladded functional surface layers
Popis výsledku anglicky
This study evaluates the fatigue life of S960 high-strength steel with laser-cladded layers of aluminium bronze, hard chrome, cobalt alloy, and stainless steel, using three-point bending tests. Our results demonstrate that while these cladded layers offer potential for enhanced surface properties, they generally reduce the material's fatigue life due to alterations in the heat-affected zone and the introduction of microstructural defects at layer interfaces. The extent of fatigue life reduction varies with the type of cladded layer, highlighting the importance of optimizing laser cladding parameters to minimize detrimental effects and improve component longevity.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20300 - Mechanical engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2024
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
ENGINEERING FAILURE ANALYSIS
ISSN
1350-6307
e-ISSN
1873-1961
Svazek periodika
164
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
11
Strana od-do
1-11
Kód UT WoS článku
001270347700001
EID výsledku v databázi Scopus
2-s2.0-85198120390