PREPARATION OF BIOCERAMIC COATINGS BY ULTRASONIC SPRAY DEPOSITION

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F00%3APU23044" target="_blank" >RIV/00216305:26210/00:PU23044 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

PREPARATION OF BIOCERAMIC COATINGS BY ULTRASONIC SPRAY DEPOSITION

Popis výsledku v původním jazyce

Ca-phosphate coatings were prepared by the ultrasonic spray deposition of aerosols arised from ceramic suspension. Hydroxyapatite suspension was prepared using the precipitation method. The reaction of aqueous solutions of calcium nitrate and ammonium hydrophosphate was kept at pH= 8,5 using an ammonium hydroxide aqueous solution. Resulting concentration of HA aqueous suspension was 9 wt %. A part of prepared suspension was mixed up with water colloidal solution SiO2 (26,6 wt %) in the weight ratio 1::1. The prepared suspensions were deposited by ultrasonic spray deposition on the surface of alumina and zirconia samples. The size of aerosol drops was the function of ultrasonic frequency, viscosity of the suspension and volume of the supplied suspension. The influence of time of deposition, rate of drying and number of deposited layers on the strucrure of coatings was studied. The coated samples were futher presintered at a temperature of 500°C and sintered at a range of temperature fro

Název v anglickém jazyce

PREPARATION OF BIOCERAMIC COATINGS BY ULTRASONIC SPRAY DEPOSITION

Popis výsledku anglicky

Ca-phosphate coatings were prepared by the ultrasonic spray deposition of aerosols arised from ceramic suspension. Hydroxyapatite suspension was prepared using the precipitation method. The reaction of aqueous solutions of calcium nitrate and ammonium hydrophosphate was kept at pH= 8,5 using an ammonium hydroxide aqueous solution. Resulting concentration of HA aqueous suspension was 9 wt %. A part of prepared suspension was mixed up with water colloidal solution SiO2 (26,6 wt %) in the weight ratio 1::1. The prepared suspensions were deposited by ultrasonic spray deposition on the surface of alumina and zirconia samples. The size of aerosol drops was the function of ultrasonic frequency, viscosity of the suspension and volume of the supplied suspension. The influence of time of deposition, rate of drying and number of deposited layers on the strucrure of coatings was studied. The coated samples were futher presintered at a temperature of 500°C and sintered at a range of temperature fro

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2000

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Junior Euromat 2000

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

428-429

Název nakladatele

Deutche Gesellschaft für Materialkunde e. V.(DGM)

Místo vydání

Lausanne, Switzerland

Místo konání akce

Lausanne

Datum konání akce

28. 8. 2000

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—