A micromechanical model of cyclic creep in brittle matrix composites under compressive loading

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F01%3APU20372" target="_blank" >RIV/00216305:26210/01:PU20372 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A micromechanical model of cyclic creep in brittle matrix composites under compressive loading

Popis výsledku v původním jazyce

Mori-Tanaka approach is used to modelling metal particulate-reinforced brittle matrix composites under cyclic compressive loading. The J2 flow theory is considered as the relevant physical law of plastic flow in inclusions. A strong constraint exerted bymatrix on inclusions causes that even the evanescent kinematical hardening rule does not predict any ratchetting of a composite. It is shown that the weakening constraint of the matrix caused by microfracture damage around inclusions is closely coupledwith the plasticity of inclusion and leads to ratchetting even when the plastic deformation of inclusions is described by an isotropic hardening rule. A detailed parametric study has revealed that ratchetting is followed by either plastic or elastic shakedown, depending on the load amplitude, composite parameters and the mean microcracks length.

Název v anglickém jazyce

A micromechanical model of cyclic creep in brittle matrix composites under compressive loading

Popis výsledku anglicky

Mori-Tanaka approach is used to modelling metal particulate-reinforced brittle matrix composites under cyclic compressive loading. The J2 flow theory is considered as the relevant physical law of plastic flow in inclusions. A strong constraint exerted bymatrix on inclusions causes that even the evanescent kinematical hardening rule does not predict any ratchetting of a composite. It is shown that the weakening constraint of the matrix caused by microfracture damage around inclusions is closely coupledwith the plasticity of inclusion and leads to ratchetting even when the plastic deformation of inclusions is described by an isotropic hardening rule. A detailed parametric study has revealed that ratchetting is followed by either plastic or elastic shakedown, depending on the load amplitude, composite parameters and the mean microcracks length.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F99%2F0829" target="_blank" >GA101/99/0829: Mikromechanika a nefenomenologické konstitutivní modely kompozitů s křehkou matricí v podmínkách víceosého nízkocyklického tlakového zatěžování</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure & Micromechanics of Fracture

ISBN

80-214-1892-3

ISSN

—

e-ISSN

—

Počet stran výsledku

13

Strana od-do

355-367

Název nakladatele

Vutium, Brno University of Technology

Místo vydání

Vutium, Brno University of Technology, Brno

Místo konání akce

Brno

Datum konání akce

27. 6. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—