Tortuous Cracks under Remote Mode I: the Statistical LEFM Approach.

Popis výsledku v původním jazyce

Principles of the statistical approach to the stability of microtortuous cracks under the remote mode I loading are presented within the framework of linear elastic fracture mechanics. The basic idea of this approach lies in the suggestion that branchingoccurs only at those sites along the crack front, where the characteristic structural parameter (grain size, interparticle distance) is comparable to or larger than the plastic zone size. By using procedures introduced in the paper, extrinsic contributiion to the fracture toughness or to the fatigue threshold can be separated from experimentally obtained KIc or &#8710;Kth values. Consequently, it enables to determine the intrinsic resistance against crack initiation and growth as a more relevant measure of materials quality. Moreover, this theory elucidates quantitatively well some interesting phenomena observed in fracture and fatigue of metallic materials.

Název v anglickém jazyce

Tortuous Cracks under Remote Mode I: the Statistical LEFM Approach.

Popis výsledku anglicky

Principles of the statistical approach to the stability of microtortuous cracks under the remote mode I loading are presented within the framework of linear elastic fracture mechanics. The basic idea of this approach lies in the suggestion that branchingoccurs only at those sites along the crack front, where the characteristic structural parameter (grain size, interparticle distance) is comparable to or larger than the plastic zone size. By using procedures introduced in the paper, extrinsic contributiion to the fracture toughness or to the fatigue threshold can be separated from experimentally obtained KIc or &#8710;Kth values. Consequently, it enables to determine the intrinsic resistance against crack initiation and growth as a more relevant measure of materials quality. Moreover, this theory elucidates quantitatively well some interesting phenomena observed in fracture and fatigue of metallic materials.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20517.30" target="_blank" >OC 517.30: Vliv segregačního zkřehnutí a strukturně indukovaného stínění na odpor proti šíření trhlin v nízkolegovaných ocelích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Zeszyty naukowe politechniki Opolskiej seria Mechanika

ISSN

1429-6055

e-ISSN

—

Svazek periodika

67

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

20

Strana od-do

277-296

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—