Antagonism in Fracture and Notch Toughness of UHSLA Steels.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F01%3APU23499" target="_blank" >RIV/00216305:26210/01:PU23499 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Antagonism in Fracture and Notch Toughness of UHSLA Steels.

Popis výsledku v původním jazyce

Values of initial fracture toughness KIc and impact absorbed energy of ultra-high strength low alloy steel were determined for 6 different heat treatments leading to 3 different mean prior austenite grain sizes dm. Fracture surfaces of all specimens, except of the standard one, exhibited intergranular morphology. The fracture toughness values increased with increasing dm whereas the absorbed energy decreased. The increase in KIc values is explained in terms of the crack driving force reduction caussed by the intergranularly induced crack tip shielding. The inverse behavior of impact test specimens is associated with a low resistance of coarse grained structures against crack nucleation. Separation of the extrinsic shielding effect from the measured KIcvalues by using a 3D model of the intergranular crack front resulted in a comparable intrinsic fracture toughness of all investigated steel grades.

Název v anglickém jazyce

Antagonism in Fracture and Notch Toughness of UHSLA Steels.

Popis výsledku anglicky

Values of initial fracture toughness KIc and impact absorbed energy of ultra-high strength low alloy steel were determined for 6 different heat treatments leading to 3 different mean prior austenite grain sizes dm. Fracture surfaces of all specimens, except of the standard one, exhibited intergranular morphology. The fracture toughness values increased with increasing dm whereas the absorbed energy decreased. The increase in KIc values is explained in terms of the crack driving force reduction caussed by the intergranularly induced crack tip shielding. The inverse behavior of impact test specimens is associated with a low resistance of coarse grained structures against crack nucleation. Separation of the extrinsic shielding effect from the measured KIcvalues by using a 3D model of the intergranular crack front resulted in a comparable intrinsic fracture toughness of all investigated steel grades.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20517.30" target="_blank" >OC 517.30: Vliv segregačního zkřehnutí a strukturně indukovaného stínění na odpor proti šíření trhlin v nízkolegovaných ocelích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Charpy Centenary Conference 2001

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

465-472

Název nakladatele

SF2M Les Fontelles

Místo vydání

Les Fontelles

Místo konání akce

Poitiers France

Datum konání akce

20. 9. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—