Propagation of a fatigue crack through a protektive layer.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F01%3APU24793" target="_blank" >RIV/00216305:26210/01:PU24793 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Propagation of a fatigue crack through a protektive layer.

Popis výsledku v původním jazyce

The contribution describes a study of the behaviour of a fatigue crack growing in a protective layer and penetrating through the interface and into the substrate. The study aims especially to quantify the influence of the interface on the rate and treshold value of a fatigue crack propagating perpendiculary to the interface. Special atention is devoted to the case of a crak touching the interface. It is shown that the fatigue crack propagation rate and the corresponding treshold value are strongly influuenced by the existence of an interface between two materials. A tentative procedure suggested in the paper makes it possible to quantify the effect and determine the dependence of a rate of propagation of a fatigue crack growing through the interface and the bi-material parameters alfa and beta. The results generaly contribute to a better understanding of the failure of structures with protective layers.

Název v anglickém jazyce

Propagation of a fatigue crack through a protektive layer.

Popis výsledku anglicky

The contribution describes a study of the behaviour of a fatigue crack growing in a protective layer and penetrating through the interface and into the substrate. The study aims especially to quantify the influence of the interface on the rate and treshold value of a fatigue crack propagating perpendiculary to the interface. Special atention is devoted to the case of a crak touching the interface. It is shown that the fatigue crack propagation rate and the corresponding treshold value are strongly influuenced by the existence of an interface between two materials. A tentative procedure suggested in the paper makes it possible to quantify the effect and determine the dependence of a rate of propagation of a fatigue crack growing through the interface and the bi-material parameters alfa and beta. The results generaly contribute to a better understanding of the failure of structures with protective layers.

Druh

C - Kapitola v odborné knize

CEP obor

JQ - Strojní zařízení a nástroje

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F99%2F0829" target="_blank" >GA101/99/0829: Mikromechanika a nefenomenologické konstitutivní modely kompozitů s křehkou matricí v podmínkách víceosého nízkocyklického tlakového zatěžování</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Surface Treatment V. Computer methods and experimental measurements.

ISBN

1-85312-872-4

Počet stran výsledku

10

Strana od-do

181-190

Počet stran knihy

—

Název nakladatele

Edited by C.A. Brebia, WIT Press 2001, Southampton, Boston

Místo vydání

Great Britain, Southampton, Boston

Kód UT WoS kapitoly

—