Hydrotermální syntéza oxidu ceričitého dopovaného prvky vzácných zemin

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F03%3APU42119" target="_blank" >RIV/00216305:26210/03:PU42119 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hydrothermal Synthesis of Ceria Doped by Rare Earth Elements

Popis výsledku v původním jazyce

The hydrothermal synthesis of cerium oxide doped by Gd3+, Sm3+ and Y3+ ions was studied. The ractions were held at temperatures of 200-250C and pressures of 150-200 bars in the presence of these bases: hydrazine, monoethanolamine, triethanolamine or ammonium hydroxide. The reaction product - cerium oxide doped by yttrium, samarium or gadolinium had the cubic crystal lattice. The size of crystallites was in the range of 5-200 nm. The crystallites formed particles with the mean size of 10-200 nm. Cerium oxide powders were shaped by uniaxial pressing and sintered at a temperature of 1500 C. Density of the sintered ceramics was in the range of 83-95 % of theoretical value and the size of the grains was in the range of 1-5 ěm. The attained results have showed that the hydrothermal synthesis is aplicable for preparations of nanocrystalline cerium oxide doped with rare elements without necessity of the high temperature calcination.

Název v anglickém jazyce

Hydrothermal Synthesis of Ceria Doped by Rare Earth Elements

Popis výsledku anglicky

The hydrothermal synthesis of cerium oxide doped by Gd3+, Sm3+ and Y3+ ions was studied. The ractions were held at temperatures of 200-250C and pressures of 150-200 bars in the presence of these bases: hydrazine, monoethanolamine, triethanolamine or ammonium hydroxide. The reaction product - cerium oxide doped by yttrium, samarium or gadolinium had the cubic crystal lattice. The size of crystallites was in the range of 5-200 nm. The crystallites formed particles with the mean size of 10-200 nm. Cerium oxide powders were shaped by uniaxial pressing and sintered at a temperature of 1500 C. Density of the sintered ceramics was in the range of 83-95 % of theoretical value and the size of the grains was in the range of 1-5 ěm. The attained results have showed that the hydrothermal synthesis is aplicable for preparations of nanocrystalline cerium oxide doped with rare elements without necessity of the high temperature calcination.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20525.10" target="_blank" >OC 525.10: Příprava a vlastnosti keramických materiálů s iontovou nebo iontově-elektronovou vodivostí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Abstract Book

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

43-43

Název nakladatele

Jožef Stefan Institute

Místo vydání

Beograd

Místo konání akce

Bled

Datum konání akce

31. 8. 2003

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—