Povlak cínu na ocelovém plechu a jeho vliv na základní mechanické vlastnosti bez přihlédnutí k orientaci vzorku

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F04%3APU47762" target="_blank" >RIV/00216305:26210/04:PU47762 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Tin coating on a steel sheet its insfluence on basic mechanical properties regardless of sample orientation
Popis výsledku v původním jazyce
This contribution deals with influence of tin coating on steel sheet mechanical properties. A sheet 0.16 mm thick provided with electrolytically applied tin coating of 2.0/2.0 gm-2 surface weight was used for experiments. This sheet was manufactured by U.S. STEEL in Košice and marked as DR 580 with the stone finish surface. Mechanical properties of coated and uncoated sheets were examined. Attention was paid to tensile strength, yield point and deep-drawing quality.
Název v anglickém jazyce
Tin coating on a steel sheet its insfluence on basic mechanical properties regardless of sample orientation
Popis výsledku anglicky
This contribution deals with influence of tin coating on steel sheet mechanical properties. A sheet 0.16 mm thick provided with electrolytically applied tin coating of 2.0/2.0 gm-2 surface weight was used for experiments. This sheet was manufactured by U.S. STEEL in Košice and marked as DR 580 with the stone finish surface. Mechanical properties of coated and uncoated sheets were examined. Attention was paid to tensile strength, yield point and deep-drawing quality.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JR - Ostatní strojírenství
OECD FORD obor
—

Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)