INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY

Popis výsledku v původním jazyce

During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number ofdegradation effects, particularly high-temperature corrosion, fatigue processes and creep. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a connstant load of temperatures ranging from 750 up to 950"aC. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods after the fracture of test bars.

Název v anglickém jazyce

INFLUENCE OF THE CREEP ON THE STRUCTURE AND PROPERTIES OF THE CAST Ni-SUPERALLOY

Popis výsledku anglicky

During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number ofdegradation effects, particularly high-temperature corrosion, fatigue processes and creep. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a connstant load of temperatures ranging from 750 up to 950"aC. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods after the fracture of test bars.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F1088" target="_blank" >GA106/02/1088: Optimalizace chemického složení a heterogenity, struktury, vlastností a užití lité niklové slitiny k výrobě spalovací turbíny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

10

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

5

Strana od-do

443-447

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—