Únavové vlastnosti ADI v závislosti na poloze zkušebního vzorku v kýlovém bloku
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F04%3APU55331" target="_blank" >RIV/00216305:26210/04:PU55331 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue Properties of ADI in Dependence on a Position of Secimen in a Keel Block
Popis výsledku v původním jazyce
The aim of this work is to complete knowledges about the fatigue behaviour of an isothermaly heat treated nodular cast iron, so-called ADI. The nodular cast iron ranks to all important branches of engineering industry already. Recently, it startsto substitute casts of grey cast iron and steel as well, even in the event of cyclically loaded components e.g gears, crankshafts or half-time shafts [1,2]. During cycling, an irreversible process of mechanical properties happens. The fatigue fraacture is initiated at an specific cycle count when the working stress is higher than the fatigue limit. For Wöhler´s curves and the fatigue limit determination is usually used a group of 12 to 15 specimens, which are removed from different places of a cast keel block.The fatigue limit of the material is influenced by many factors, which count defects as shrinkage porosity and impurities as well, which are formed during casting. For correct determination of mechanical properties, th
Název v anglickém jazyce
Fatigue Properties of ADI in Dependence on a Position of Secimen in a Keel Block
Popis výsledku anglicky
The aim of this work is to complete knowledges about the fatigue behaviour of an isothermaly heat treated nodular cast iron, so-called ADI. The nodular cast iron ranks to all important branches of engineering industry already. Recently, it startsto substitute casts of grey cast iron and steel as well, even in the event of cyclically loaded components e.g gears, crankshafts or half-time shafts [1,2]. During cycling, an irreversible process of mechanical properties happens. The fatigue fraacture is initiated at an specific cycle count when the working stress is higher than the fatigue limit. For Wöhler´s curves and the fatigue limit determination is usually used a group of 12 to 15 specimens, which are removed from different places of a cast keel block.The fatigue limit of the material is influenced by many factors, which count defects as shrinkage porosity and impurities as well, which are formed during casting. For correct determination of mechanical properties, th
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F03%2F1265" target="_blank" >GA106/03/1265: Vliv vybraných faktorů na únavové vlastnosti izotermicky zušlechtěné tvárné litiny</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
2nd Internacional PhD Conference on Mechanical Engineering
ISBN
80-7043-330-2
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
37-40
Název nakladatele
TYPOS-digital print
Místo vydání
Plzeň
Místo konání akce
Srní
Datum konání akce
8. 11. 2004
Typ akce podle státní příslušnosti
CST - Celostátní akce
Kód UT WoS článku
—