Effect of thermal expansion mismatches of matrix and fibres on microcracking of brittle matrix composites

Popis výsledku v původním jazyce

There is investigated a crack problem for an array of collinear microcracks in composite matrix. Inclusions are situated in between the neighbouring microcracks tips and exhibit different elastic properties than matrix. The problem is solved using the technique of distributed dislocations. Stress intensity factor is calculated for various cracks/inclusions geometries and elastic moduli mismatches. The process by which a fibre-reinforced cross-ply ceramic composite is damaged and eventually fails under ttension is very complex. After an initial elastic response, the damage starts with matrix cracking in 90° plies. These microcracks spread as 3D tunnelling cracks from small flaws located in the matrix of the 90° plies. Driving force for steady-state tunnelling, Gss, can be calculated using plane-strain elasticity solutions for the energy release rate G at the edge of plane-strain crack.

Název v anglickém jazyce

Effect of thermal expansion mismatches of matrix and fibres on microcracking of brittle matrix composites

Popis výsledku anglicky

There is investigated a crack problem for an array of collinear microcracks in composite matrix. Inclusions are situated in between the neighbouring microcracks tips and exhibit different elastic properties than matrix. The problem is solved using the technique of distributed dislocations. Stress intensity factor is calculated for various cracks/inclusions geometries and elastic moduli mismatches. The process by which a fibre-reinforced cross-ply ceramic composite is damaged and eventually fails under ttension is very complex. After an initial elastic response, the damage starts with matrix cracking in 90° plies. These microcracks spread as 3D tunnelling cracks from small flaws located in the matrix of the 90° plies. Driving force for steady-state tunnelling, Gss, can be calculated using plane-strain elasticity solutions for the energy release rate G at the edge of plane-strain crack.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP101%2F05%2FP290" target="_blank" >GP101/05/P290: Výpočet lomově mechanických parametrů pro trhliny v anisotropních bimateriálových prostředích pomocí techniky spojitě rozdělených dislokací</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Aplikovaná mechanika 2005

ISBN

80-214-2373-0

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

85-86

Název nakladatele

ÚMTMB FSI v Brně

Místo vydání

Brno

Místo konání akce

Hrotovice

Datum konání akce

29. 3. 2005

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—