Regression Functions for Transition Curves
Popis výsledku v původním jazyce
Loaded materials can fail by rapid fracture at stresses much below their strength level as determined in tests on carefully prepated specimens. To ensure fracture-safe design in the materials , the transition-temperature approach is often used. One of the experimental possibilities determining transition temperature isn the Charpy impact test, when a notched-bar speciamen is loaded in bending by a swinging pendulum and the energy absorbed in the fracturing specimen is measured. Impact energy vs. temperaature curve called transitioncurve is divided into three regions : the region of lower temperatures with brittle fracture and low values of absorbed energy (lower shelf), the transition region, and the region of higher temperatures with ductile fractureand high values of absorbed energy (higher shelf). Often also the lateral expansion of broken bars and percentage of brittle (or ductile) fracture surface is measured.
Název v anglickém jazyce
Regression Functions for Transition Curves
Popis výsledku anglicky
Loaded materials can fail by rapid fracture at stresses much below their strength level as determined in tests on carefully prepated specimens. To ensure fracture-safe design in the materials , the transition-temperature approach is often used. One of the experimental possibilities determining transition temperature isn the Charpy impact test, when a notched-bar speciamen is loaded in bending by a swinging pendulum and the energy absorbed in the fracturing specimen is measured. Impact energy vs. temperaature curve called transitioncurve is divided into three regions : the region of lower temperatures with brittle fracture and low values of absorbed energy (lower shelf), the transition region, and the region of higher temperatures with ductile fractureand high values of absorbed energy (higher shelf). Often also the lateral expansion of broken bars and percentage of brittle (or ductile) fracture surface is measured.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F03%2F1265" target="_blank" >GA106/03/1265: Vliv vybraných faktorů na únavové vlastnosti izotermicky zušlechtěné tvárné litiny</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2005
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Zeszyty naukowe politechniki Opolskiej seria Mechanika
ISSN
1429-6055
e-ISSN
—
Svazek periodika
86
Číslo periodika v rámci svazku
308
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
5
Strana od-do
241-245
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—