Zpracování středně uhlíkové oceli metodou ECAP

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU68292" target="_blank" >RIV/00216305:26210/05:PU68292 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Processing of medium carbon steel by hot pressing prior ECAP

Popis výsledku v původním jazyce

Medium carbon steel prior to subjecting severe plastic deformation was thermomechanically treated in order to modified the initial grain size and morphology of cementite particles. The further structure modification of the steel was obtained during the equal channel angular pressing at increased temperature using the effective strain 3. The thermal stability qnd mechanical properties of the deformed steel were related to ultrafine grained structure development. Medium carbon steel prior to subjecting severe plastic deformation was thermomechanically treated in order to modified the initial grain size and morphology of cementite particles. The further structure modification of the steel was obtained during the equal channel angular pressing at increasedtemperature using the effective strain 3. The thermal stability qnd mechanical properties of the deformed steel were related to ultrafine grained structure development. Medium carbon steel prior to subjecting severe plastic deformation w

Název v anglickém jazyce

Processing of medium carbon steel by hot pressing prior ECAP

Popis výsledku anglicky

Medium carbon steel prior to subjecting severe plastic deformation was thermomechanically treated in order to modified the initial grain size and morphology of cementite particles. The further structure modification of the steel was obtained during the equal channel angular pressing at increased temperature using the effective strain 3. The thermal stability qnd mechanical properties of the deformed steel were related to ultrafine grained structure development. Medium carbon steel prior to subjecting severe plastic deformation was thermomechanically treated in order to modified the initial grain size and morphology of cementite particles. The further structure modification of the steel was obtained during the equal channel angular pressing at increasedtemperature using the effective strain 3. The thermal stability qnd mechanical properties of the deformed steel were related to ultrafine grained structure development. Medium carbon steel prior to subjecting severe plastic deformation w

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LA%20202" target="_blank" >LA 202: Účast ČSNMT v práci FEMS a světových materiálových společností</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

JOM

ISSN

1047-4838

e-ISSN

—

Svazek periodika

57

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

2

Strana od-do

231-232

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—