Post-impact compressive load carrying capacity of fibre-metal laminate plates
Popis výsledku v původním jazyce
Compression buckling and postbuckling behaviour of fibre-metal laminate plates with a single delamination has been investigated in order to estimate the compressive load carrying capacity of such plates. Drop-weight impact tests were performed to inducedelaminations in fibre-metal laminate plates and subsequent ultrasonic inspection provided the contours of delaminated regions. These shapes of delaminations together with circular delamination shape were employed in the following finite element simulations of compressively loaded delaminated plates. Two load-limiting events were considered: yielding of metal layers and delamination growth initiation. It was found, that delaminations were not likely to grow before the onset of plastic deformation. The effect of delamination shape and buckling mode shape on the energy release rate values is also discussed.
Název v anglickém jazyce
Post-impact compressive load carrying capacity of fibre-metal laminate plates
Popis výsledku anglicky
Compression buckling and postbuckling behaviour of fibre-metal laminate plates with a single delamination has been investigated in order to estimate the compressive load carrying capacity of such plates. Drop-weight impact tests were performed to inducedelaminations in fibre-metal laminate plates and subsequent ultrasonic inspection provided the contours of delaminated regions. These shapes of delaminations together with circular delamination shape were employed in the following finite element simulations of compressively loaded delaminated plates. Two load-limiting events were considered: yielding of metal layers and delamination growth initiation. It was found, that delaminations were not likely to grow before the onset of plastic deformation. The effect of delamination shape and buckling mode shape on the energy release rate values is also discussed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA101%2F05%2F0320" target="_blank" >GA101/05/0320: Řešení obecných koncentrátorů napětí v anisotropních heterogenních prostředích pomocí kombinace MKP a techniky spojitě rozložených dislokací</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Engineering mechanics 2006
ISBN
80-86246-27-2
ISSN
—
e-ISSN
—
Počet stran výsledku
2
Strana od-do
270-271
Název nakladatele
Institute of Thermomechanics, Academy of Sciences of the Czech Republic
Místo vydání
Svratka, CZ
Místo konání akce
Svratka
Datum konání akce
15. 5. 2006
Typ akce podle státní příslušnosti
CST - Celostátní akce
Kód UT WoS článku
—