Sintering of gadolinia-doped ceria prepared by mechanochemical synthesis
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F07%3APU64439" target="_blank" >RIV/00216305:26210/07:PU64439 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Sintering of gadolinia-doped ceria prepared by mechanochemical synthesis
Popis výsledku v původním jazyce
Gadolinia-doped ceria (GDC) ceramics were prepared by mechanochemical synthesis of ceria and gadolinia (10mol.%) powders with subsequent uniaxial pressing and pressureless sintering. The mechanochemical synthesis was conducted in an attritor with different dispersion media: neutral (distilled water), basic (aqueous solution of ammonia), acidic (aqueous solution of propionic acid), and non-polar medium (xylene with stearic acid). The effect of suspension composition and attritor milling time on the sintering behaviour and ionic conductivity of GDC was studied. An attritor milling time of 3 to 6 hours was evaluated as the optimum milling time from the viewpoint of further sintering behaviour. Longer milling times resulted in nanometre-sized powders, whose sintering behaviour deteriorated due to powder agglomeration. The appearance of agglomerates in the non-polar medium was reduced. The ionic conductivity of the samples was evaluated by impedance spectroscopy and correlated with their mi
Název v anglickém jazyce
Sintering of gadolinia-doped ceria prepared by mechanochemical synthesis
Popis výsledku anglicky
Gadolinia-doped ceria (GDC) ceramics were prepared by mechanochemical synthesis of ceria and gadolinia (10mol.%) powders with subsequent uniaxial pressing and pressureless sintering. The mechanochemical synthesis was conducted in an attritor with different dispersion media: neutral (distilled water), basic (aqueous solution of ammonia), acidic (aqueous solution of propionic acid), and non-polar medium (xylene with stearic acid). The effect of suspension composition and attritor milling time on the sintering behaviour and ionic conductivity of GDC was studied. An attritor milling time of 3 to 6 hours was evaluated as the optimum milling time from the viewpoint of further sintering behaviour. Longer milling times resulted in nanometre-sized powders, whose sintering behaviour deteriorated due to powder agglomeration. The appearance of agglomerates in the non-polar medium was reduced. The ionic conductivity of the samples was evaluated by impedance spectroscopy and correlated with their mi
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/OC%20102" target="_blank" >OC 102: Příprava elektrokeramiky z nanoprášků</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of the European Ceramic Society
ISSN
0955-2219
e-ISSN
—
Svazek periodika
27
Číslo periodika v rámci svazku
13-15
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000248822800163
EID výsledku v databázi Scopus
—