Mikrovlnná syntéza oxidu bismutitého

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F07%3APU70544" target="_blank" >RIV/00216305:26210/07:PU70544 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mirowave-assisted synthesis of bismuth oxide

Popis výsledku v původním jazyce

Single phase and ultrafine bismuth oxide was synthesized via microwave-assisted hydrothermal synthesis. The effect of reaction parameters (temperature/pressure and pH) on the product phase composition and morphology was discussed. The transformation of bismuth hydroxide into bismuth oxide was controlled by pH value and it was accelerated by time and temperature. The phase composition of reaction products was strongly dependent on pH value. The amorphous products were obtained at acidic pH conditions andthe crystalline single phase product ?-Bi2O3 phase was obtained at pH ?12. The particle size was reduced from micrometric to nanometric size in the presence of the chelating agent. The bismuth hydroxides into bismuth oxides transformation mechanism, consisting in polycondensation of Bi - OH bounds to Bi - O - Bi bridges and crystallization of Bi2O3, was proposed.

Název v anglickém jazyce

Mirowave-assisted synthesis of bismuth oxide

Popis výsledku anglicky

Single phase and ultrafine bismuth oxide was synthesized via microwave-assisted hydrothermal synthesis. The effect of reaction parameters (temperature/pressure and pH) on the product phase composition and morphology was discussed. The transformation of bismuth hydroxide into bismuth oxide was controlled by pH value and it was accelerated by time and temperature. The phase composition of reaction products was strongly dependent on pH value. The amorphous products were obtained at acidic pH conditions andthe crystalline single phase product ?-Bi2O3 phase was obtained at pH ?12. The particle size was reduced from micrometric to nanometric size in the presence of the chelating agent. The bismuth hydroxides into bismuth oxides transformation mechanism, consisting in polycondensation of Bi - OH bounds to Bi - O - Bi bridges and crystallization of Bi2O3, was proposed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20D32.001" target="_blank" >OC D32.001: Ultrazvukové sonochemické sol-gel syntézy nanometrických oxidových částic a solů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Processing and Application of Ceramics

ISSN

1820-6131

e-ISSN

—

Svazek periodika

1

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

CS - Srbsko a Černá Hora

Počet stran výsledku

5

Strana od-do

29-33

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—