INFLUECNE OF TEMPERATURE DIFFERENCES OF MIXED STREAMS UPON T-JUNCTION DAMAGE
Popis výsledku v původním jazyce
The problem of thermal fatigue in pipe connections under the influence of streams mixing is one of the most discussed problems on international conferences. Numerous failures occur in industry as a result of this damage mechanism. It is caused by frequent stress changes developed by an effect of non-stationary thermal fields. The degree of damage is greatly dependent on characteristic of material, geometrical design of a pipe connection in operational conditions. The report is dealing with influence oftemperature differences of mixing media streams upon pipe material damage cumulation. It is focused on a perpendicular T-junction made of ferritic steel, which is protected inside with an anticorrosive weld deposit from austenitic steel. Six cases of temperature differences will be considered for particular operational conditions with a step of 50 centigrade, and the damage cumulation process will be observed. Thanks to it, it will be possible to judge better the meaning of streams tempe
Název v anglickém jazyce
INFLUECNE OF TEMPERATURE DIFFERENCES OF MIXED STREAMS UPON T-JUNCTION DAMAGE
Popis výsledku anglicky
The problem of thermal fatigue in pipe connections under the influence of streams mixing is one of the most discussed problems on international conferences. Numerous failures occur in industry as a result of this damage mechanism. It is caused by frequent stress changes developed by an effect of non-stationary thermal fields. The degree of damage is greatly dependent on characteristic of material, geometrical design of a pipe connection in operational conditions. The report is dealing with influence oftemperature differences of mixing media streams upon pipe material damage cumulation. It is focused on a perpendicular T-junction made of ferritic steel, which is protected inside with an anticorrosive weld deposit from austenitic steel. Six cases of temperature differences will be considered for particular operational conditions with a step of 50 centigrade, and the damage cumulation process will be observed. Thanks to it, it will be possible to judge better the meaning of streams tempe
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CI - Průmyslová chemie a chemické inženýrství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Engineering Mechanics
ISSN
1802-1484
e-ISSN
—
Svazek periodika
15
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
8
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—