Low-Temperature and High -Temperature Anomalies in Temperature Shift of Stress - Lifetime Fatigue Curves

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F08%3APU78173" target="_blank" >RIV/00216305:26210/08:PU78173 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Low-Temperature and High -Temperature Anomalies in Temperature Shift of Stress - Lifetime Fatigue Curves

Popis výsledku v původním jazyce

Most families of S-N curves determined at various temperatures present certain general regularities on whose basis the Basquin equation describing finite-life S-N curves can be generalized for various temperatures. This equation can be represented by straight lines with common slope if log-log fit for stress vs. temperature dependence is used. Deviations from these straight lines (anomalies) are evidence that additional degradation mechanisms are effective besides fatigue, whose temperature dependencesdiffer from the mentioned temperature dependence of fatigue strength. In high-temperature region it is most often cyclic creep, in low-temperature region atermal processec of plastic deformation can play significant role in fatigue failure.

Název v anglickém jazyce

Low-Temperature and High -Temperature Anomalies in Temperature Shift of Stress - Lifetime Fatigue Curves

Popis výsledku anglicky

Most families of S-N curves determined at various temperatures present certain general regularities on whose basis the Basquin equation describing finite-life S-N curves can be generalized for various temperatures. This equation can be represented by straight lines with common slope if log-log fit for stress vs. temperature dependence is used. Deviations from these straight lines (anomalies) are evidence that additional degradation mechanisms are effective besides fatigue, whose temperature dependencesdiffer from the mentioned temperature dependence of fatigue strength. In high-temperature region it is most often cyclic creep, in low-temperature region atermal processec of plastic deformation can play significant role in fatigue failure.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F1265" target="_blank" >GA106/03/1265: Vliv vybraných faktorů na únavové vlastnosti izotermicky zušlechtěné tvárné litiny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science Forum

ISSN

0255-5476

e-ISSN

—

Svazek periodika

567-568

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—