Effect of Temperature on cyclic stress components of Inconel 738LC superalloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F08%3APU87819" target="_blank" >RIV/00216305:26210/08:PU87819 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of Temperature on cyclic stress components of Inconel 738LC superalloy

Popis výsledku v původním jazyce

Multiple step tests in strain control havebeen performed on cylindrical specimens of cast polycrastalline Inconel 738LC superalloy at 23, 500 and 800 C in laboratory atmosphere to study the effect of temperature on the internal and effective cyclic stress components. At these temperatures, the evolution of the effective and internal stress components and effective elastic modules were derived from the hysteresis loops which were analysed according to the statistical theory of hysteresis loop. Cyclic hardening/softening curves and shortened cyclic stress-strain curves were obtained at three temperatures. Cyclic hardening/softening behaviour depends both on temperature and strain amplitude. Low amplitude straining was characterized by saturation of the stress amplitude. In high amplitude straining a pronounced hardening was found at room temperature and at 500 C. Saturated behaviour was found at temperature 800 C. The shortened cyclic stress-strain curves can be fitted by power law at th

Název v anglickém jazyce

Effect of Temperature on cyclic stress components of Inconel 738LC superalloy

Popis výsledku anglicky

Multiple step tests in strain control havebeen performed on cylindrical specimens of cast polycrastalline Inconel 738LC superalloy at 23, 500 and 800 C in laboratory atmosphere to study the effect of temperature on the internal and effective cyclic stress components. At these temperatures, the evolution of the effective and internal stress components and effective elastic modules were derived from the hysteresis loops which were analysed according to the statistical theory of hysteresis loop. Cyclic hardening/softening curves and shortened cyclic stress-strain curves were obtained at three temperatures. Cyclic hardening/softening behaviour depends both on temperature and strain amplitude. Low amplitude straining was characterized by saturation of the stress amplitude. In high amplitude straining a pronounced hardening was found at room temperature and at 500 C. Saturated behaviour was found at temperature 800 C. The shortened cyclic stress-strain curves can be fitted by power law at th

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F1507" target="_blank" >GA106/07/1507: Interakce nízkocyklové únavy a creepu u moderních vysokoteplotních konstrukčních materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of 17th European Conference on Fracture

ISBN

9781617823190

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

1358-1365

Název nakladatele

VUTIUM

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

2. 9. 2008

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—