Popis výsledku v původním jazyce

Reoxidation of steel is a term for summary designation of secondary and tertiary oxidation of steel occurring during keeping the metal in a ladle after tapping it from a furnace and during casting in a mould cavity. During reoxidation the oxygen concentration and its activity in a casting are growing. In case that oxygen activity exceeds the equilibrium activity of oxygen with carbon the casting part or the whole casting can be afflicted with gas cavities of carbon monoxide. With higher oxygen activitythe formations of oxides of elements with lower deoxidation ability (Mn, Si) continues. Those oxides can form in castings the extensive slaggy formations in their volume or on the casting surface designated as secondary slag inclusions. Thus the steel reoxidation directly influences surface and internal quality of steel castings and consequently the manufacturing costs too.

Název v anglickém jazyce

EXPERIMENTAL VERIFICATION OF A MODEL OF STEEL REOXIDATION

Popis výsledku anglicky

Reoxidation of steel is a term for summary designation of secondary and tertiary oxidation of steel occurring during keeping the metal in a ladle after tapping it from a furnace and during casting in a mould cavity. During reoxidation the oxygen concentration and its activity in a casting are growing. In case that oxygen activity exceeds the equilibrium activity of oxygen with carbon the casting part or the whole casting can be afflicted with gas cavities of carbon monoxide. With higher oxygen activitythe formations of oxides of elements with lower deoxidation ability (Mn, Si) continues. Those oxides can form in castings the extensive slaggy formations in their volume or on the casting surface designated as secondary slag inclusions. Thus the steel reoxidation directly influences surface and internal quality of steel castings and consequently the manufacturing costs too.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA5%2F048" target="_blank" >FT-TA5/048: Predikce a odstranění vnitřních a povrchových vad produktů slévárenské výroby</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Transaction of the VŠB-Technical university of Ostrava, Mechanical series

ISSN

1210-0471

e-ISSN

—

Svazek periodika

52

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—