FATIGUE BEHAVIOUR OF AZ91 MAGNESIUM ALLOY

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU85233" target="_blank" >RIV/00216305:26210/09:PU85233 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

FATIGUE BEHAVIOUR OF AZ91 MAGNESIUM ALLOY

Popis výsledku v původním jazyce

The paper deals with the determination of principal mechanical properties and the investigation of fatigue behaviour of AZ91 magnesium alloy. The experimental material was made by squeeze casting technique and heat treated to obtain T4 state (solution annealing), when hard, brittle Mg17Al12 intermetallic phase is dissolved. The basic mechanical properties (Young's modulus, ultimate tensile strength, yield strength, elongation to fracture and reduction of area) were determinated by static tensile test. Furthermore, fatigue parameters were investigated and standard tensile curve was compared with cyclic stress-strain curve. The comparison indicates that studied material exhibited cyclic hardening at whole lifetime. In addition, the S-N curve on the basisof smooth test bars tested under symmetrical push-pull loading at room temperature was evaluated. The measured data were subsequently used for assessing the Manson-Coffin curve and for fitting with suitable regression function for determ

Název v anglickém jazyce

FATIGUE BEHAVIOUR OF AZ91 MAGNESIUM ALLOY

Popis výsledku anglicky

The paper deals with the determination of principal mechanical properties and the investigation of fatigue behaviour of AZ91 magnesium alloy. The experimental material was made by squeeze casting technique and heat treated to obtain T4 state (solution annealing), when hard, brittle Mg17Al12 intermetallic phase is dissolved. The basic mechanical properties (Young's modulus, ultimate tensile strength, yield strength, elongation to fracture and reduction of area) were determinated by static tensile test. Furthermore, fatigue parameters were investigated and standard tensile curve was compared with cyclic stress-strain curve. The comparison indicates that studied material exhibited cyclic hardening at whole lifetime. In addition, the S-N curve on the basisof smooth test bars tested under symmetrical push-pull loading at room temperature was evaluated. The measured data were subsequently used for assessing the Manson-Coffin curve and for fitting with suitable regression function for determ

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/1M0556" target="_blank" >1M0556: Ekocentrum aplikovaného výzkumu neželezných kovů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Transaction of the VŠB-Technical university of Ostrava, Mechanical series

ISSN

1210-0471

e-ISSN

—

Svazek periodika

2009

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—