Influence of Surface Texturing on Lubricant Film Formation and Surface Fatigue

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F10%3APU87037" target="_blank" >RIV/00216305:26210/10:PU87037 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Surface Texturing on Lubricant Film Formation and Surface Fatigue

Popis výsledku v původním jazyce

This paper concerns a study of the lubricant film formation and behavior of a point contact under non-steady state conditions. Transient Elastohydrodynamic (EHD) lubrication, where operating parameters such as speed and load vary over time, occurs in many machine elements including cams, gears and roller bearings. Therefore, an attention in last few years was focused on behavior and formation of a lubricant film in Elastohydrodynamic lubricated (EHL) contact under non-steady state conditions. The critical running sequences of EHL contacts include e.g. starting or halting of contact surfaces and also abrupt increases or decreases of surface speed and load. These cases can cause a rupture of a lubricant film and in consequence of this action also damageof contact surfaces. This study is devoted to the experimental research of the behavior of EHD films during reversal of entrainment in reciprocating motion. Moreover influence of surface texturing on rolling contact fatigue life of rubbin

Název v anglickém jazyce

Influence of Surface Texturing on Lubricant Film Formation and Surface Fatigue

Popis výsledku anglicky

This paper concerns a study of the lubricant film formation and behavior of a point contact under non-steady state conditions. Transient Elastohydrodynamic (EHD) lubrication, where operating parameters such as speed and load vary over time, occurs in many machine elements including cams, gears and roller bearings. Therefore, an attention in last few years was focused on behavior and formation of a lubricant film in Elastohydrodynamic lubricated (EHL) contact under non-steady state conditions. The critical running sequences of EHL contacts include e.g. starting or halting of contact surfaces and also abrupt increases or decreases of surface speed and load. These cases can cause a rupture of a lubricant film and in consequence of this action also damageof contact surfaces. This study is devoted to the experimental research of the behavior of EHD films during reversal of entrainment in reciprocating motion. Moreover influence of surface texturing on rolling contact fatigue life of rubbin

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JR - Ostatní strojírenství

OECD FORD obor

—

Projekt

<a href="/cs/project/GC101%2F09%2FJ003" target="_blank" >GC101/09/J003: Experimentální studium elastohydrodynamického a smíšeného mazání hypoidních převodů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Mechanics

ISSN

1802-1484

e-ISSN

—

Svazek periodika

17

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

10

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—