Structural Characterisation of Particles Created in Al-Ni Composites at Moderate Temperatueres

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F10%3APU87140" target="_blank" >RIV/00216305:26210/10:PU87140 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structural Characterisation of Particles Created in Al-Ni Composites at Moderate Temperatueres

Popis výsledku v původním jazyce

Aluminium matrix composites were prepared by HVOF spraying of nickel with 20 wt.% chromium powders onto the aluminium sheet's surface followed by annealing at the temperature 600oC and 630oC. At the interface between the original coating and aluminium matrix the layers containing the Al3Ni2 and Al3Ni intermediate phase compositions were created. Moreover nickel without the assistance of chromium diffuse into the aluminium matrix and causes stenghtening by stable Al3Ni and metastable Al9Ni2 particles. The microstructures were obtained by scanning electron microscope (SEM) and transmission electron microscope (TEM). Chemical compositions were estimated by energy dispersive microanalysis. The TEM diffraction patterns were evaluated using JEMS software.

Název v anglickém jazyce

Structural Characterisation of Particles Created in Al-Ni Composites at Moderate Temperatueres

Popis výsledku anglicky

Aluminium matrix composites were prepared by HVOF spraying of nickel with 20 wt.% chromium powders onto the aluminium sheet's surface followed by annealing at the temperature 600oC and 630oC. At the interface between the original coating and aluminium matrix the layers containing the Al3Ni2 and Al3Ni intermediate phase compositions were created. Moreover nickel without the assistance of chromium diffuse into the aluminium matrix and causes stenghtening by stable Al3Ni and metastable Al9Ni2 particles. The microstructures were obtained by scanning electron microscope (SEM) and transmission electron microscope (TEM). Chemical compositions were estimated by energy dispersive microanalysis. The TEM diffraction patterns were evaluated using JEMS software.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F09%2FP513" target="_blank" >GP106/09/P513: Nekonvenční metody pro přípravu kompozitních materiálů sendvičového typu na bázi Al</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta metalurgica slovaca

ISSN

1338-1660

e-ISSN

—

Svazek periodika

2010

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—