Local Aspects of Shear-Mode Crack Propagation in Austenitic Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F10%3APU87439" target="_blank" >RIV/00216305:26210/10:PU87439 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Local Aspects of Shear-Mode Crack Propagation in Austenitic Steel

Popis výsledku v původním jazyce

An original and efficient testing setup has been designed in collaboration of the Institut of Physical Engineering and the Erich-Schmid Institute of Materials Science in Leoben. This device allows simultaneous fatigue crack propagation in pure shear modes II and III in a single specimen. The specimens were made of austenitic (x5NiCrTi26-15) steel and loaded under shear stress range from 80 MPa to 220 MPa with loading ratio R = 0.1. The stereophotogrammetrical reconstruction of the fracture surface morphology in the scanning electron microscope was performed. The analysis showed that the 3D topology of factory-roof patterns in torsion loading is very similar to that identified in the case of cyclic shear loading.

Název v anglickém jazyce

Local Aspects of Shear-Mode Crack Propagation in Austenitic Steel

Popis výsledku anglicky

An original and efficient testing setup has been designed in collaboration of the Institut of Physical Engineering and the Erich-Schmid Institute of Materials Science in Leoben. This device allows simultaneous fatigue crack propagation in pure shear modes II and III in a single specimen. The specimens were made of austenitic (x5NiCrTi26-15) steel and loaded under shear stress range from 80 MPa to 220 MPa with loading ratio R = 0.1. The stereophotogrammetrical reconstruction of the fracture surface morphology in the scanning electron microscope was performed. The analysis showed that the 3D topology of factory-roof patterns in torsion loading is very similar to that identified in the case of cyclic shear loading.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/2E08017" target="_blank" >2E08017: Postupy a metody pro zvýšení počtu pracovníků ve vědě a výzkumu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemické listy

ISSN

0009-2770

e-ISSN

—

Svazek periodika

104

Číslo periodika v rámci svazku

15

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—