Checking the metallurgy with the aid of inclusion analysis
Popis výsledku v původním jazyce
Results of studying the influence of inclusion morphology on properties of heavy casting are given. The inclusion morphology is dependent on content and kind of the deoxidizing element. Due to segregations the inclusions can be formed in heavy castings under different conditions (by concentration of deoxidizing elements) than in castings of common size. In heavy casting during deoxidation the inclusions of the IVth type occur more frequently. Deoxidation with zirconium shows to be for some heavy casting unsuitable one. Similarly in castings deoxidized with cerium and lanthanum the inclusions of greater sizes occur that can unfavourably influence the steel properties and increase the tendency to crack formation. The inclusion morphology after deoxidation with magnesium is also unsuitable for heavy castings.
Název v anglickém jazyce
Checking the metallurgy with the aid of inclusion analysis
Popis výsledku anglicky
Results of studying the influence of inclusion morphology on properties of heavy casting are given. The inclusion morphology is dependent on content and kind of the deoxidizing element. Due to segregations the inclusions can be formed in heavy castings under different conditions (by concentration of deoxidizing elements) than in castings of common size. In heavy casting during deoxidation the inclusions of the IVth type occur more frequently. Deoxidation with zirconium shows to be for some heavy casting unsuitable one. Similarly in castings deoxidized with cerium and lanthanum the inclusions of greater sizes occur that can unfavourably influence the steel properties and increase the tendency to crack formation. The inclusion morphology after deoxidation with magnesium is also unsuitable for heavy castings.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI1%2F070" target="_blank" >FR-TI1/070: Výzkum a optimalizace technologie výroby masivních ocelových odlitků</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Archives of foundry engineering
ISSN
1897-3310
e-ISSN
—
Svazek periodika
11
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
5
Strana od-do
118-122
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—