A BREAKOUT OF A SLAB AFTER QUICK CHANGING THE TUNDISH AND STEEL QUALITY

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU92527" target="_blank" >RIV/00216305:26210/11:PU92527 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/11:86080749

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A BREAKOUT OF A SLAB AFTER QUICK CHANGING THE TUNDISH AND STEEL QUALITY

Popis výsledku v původním jazyce

An important area of the caster is the so-called secondary cooling zone, which is subdivided into thirteen sections. In the secondary-cooling zone, where the slab is beginning to straighten out the breakout of the steel can occur in points of increased local chemical and temperature heterogeneity of the steel, from increased tension as a result of the bending of the slab and also from a high local concentration of non-metal, slag inclusions. Especially dangerous are the changes in the chemical composition of the steel during the actual concasting. In the case of two melts one immediately after the other, i.e. when melt of steel of quality A finished and right now the melt of quality B followed, this could lead to interruption in the concasting and a breakout. The material, physical, chemical and technological parameters, which both melts differed in were determined. The parameters from the temperature field were calculated by means of the model, for example maximal and minimal lenghts

Název v anglickém jazyce

A BREAKOUT OF A SLAB AFTER QUICK CHANGING THE TUNDISH AND STEEL QUALITY

Popis výsledku anglicky

An important area of the caster is the so-called secondary cooling zone, which is subdivided into thirteen sections. In the secondary-cooling zone, where the slab is beginning to straighten out the breakout of the steel can occur in points of increased local chemical and temperature heterogeneity of the steel, from increased tension as a result of the bending of the slab and also from a high local concentration of non-metal, slag inclusions. Especially dangerous are the changes in the chemical composition of the steel during the actual concasting. In the case of two melts one immediately after the other, i.e. when melt of steel of quality A finished and right now the melt of quality B followed, this could lead to interruption in the concasting and a breakout. The material, physical, chemical and technological parameters, which both melts differed in were determined. The parameters from the temperature field were calculated by means of the model, for example maximal and minimal lenghts

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2011 Conference Proceedings, (CD ROM Paper 775)

ISBN

978-80-87294-24-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

99-104

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

18. 5. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—