Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU96268" target="_blank" >RIV/00216305:26210/11:PU96268 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/11:00361095

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region

Popis výsledku v původním jazyce

Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 10^8 to 2x10^10 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.

Název v anglickém jazyce

Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region

Popis výsledku anglicky

Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 10^8 to 2x10^10 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F2001" target="_blank" >GAP108/10/2001: Cyklická plastická deformace a únavové vlastnosti ultrajemnozrnných materiálů</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering A

ISSN

0921-5093

e-ISSN

—

Svazek periodika

528

Číslo periodika v rámci svazku

22

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

7036-7040

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—