Osmotic drying of gelcast bodies in liquid desiccant

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU96346" target="_blank" >RIV/00216305:26210/11:PU96346 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Osmotic drying of gelcast bodies in liquid desiccant

Popis výsledku v původním jazyce

Osmotic drying of gelcast alumina bodies was carried out in water solutions of various polyethylene glycols (PEGs) with molecular weight ranging from 1000 to 80000 g/mol. Up to 30 % of the water content could be removed from the gelcast bodies immersed in a 43 wt% solution of PEG 80000. It was found that PEG 1000 was a less effective desiccant than the PEGs with higher molecular weights, even if the osmotic pressure was similar (4.9 MPa). The smaller PEG molecules penetrated the gelled bodies and reduced the dewatering. Moreover, the penetrated PEG molecules affected the pore structure of green bodies and in this way influenced the sintering behaviour. The time dependence of dewatering and the effect of the size of gelcast bodies were investigated andcorrelated with the green body structure and sintering behaviour in order to optimize the osmotic drying process

Název v anglickém jazyce

Osmotic drying of gelcast bodies in liquid desiccant

Popis výsledku anglicky

Osmotic drying of gelcast alumina bodies was carried out in water solutions of various polyethylene glycols (PEGs) with molecular weight ranging from 1000 to 80000 g/mol. Up to 30 % of the water content could be removed from the gelcast bodies immersed in a 43 wt% solution of PEG 80000. It was found that PEG 1000 was a less effective desiccant than the PEGs with higher molecular weights, even if the osmotic pressure was similar (4.9 MPa). The smaller PEG molecules penetrated the gelled bodies and reduced the dewatering. Moreover, the penetrated PEG molecules affected the pore structure of green bodies and in this way influenced the sintering behaviour. The time dependence of dewatering and the effect of the size of gelcast bodies were investigated andcorrelated with the green body structure and sintering behaviour in order to optimize the osmotic drying process

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC09040" target="_blank" >OC09040: Reologické chování polymerních tavenin a roztoků obsahujících nanočásticová plniva</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

31

Číslo periodika v rámci svazku

14

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

2519-2524

Kód UT WoS článku

000294935100015

EID výsledku v databázi Scopus

—