Transparent Tetragonal Yttria-Stabilized Zirconia Ceramic: Influence of Scattering Caused by Birefringence

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU96471" target="_blank" >RIV/00216305:26210/11:PU96471 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Transparent Tetragonal Yttria-Stabilized Zirconia Ceramic: Influence of Scattering Caused by Birefringence

Popis výsledku v původním jazyce

The correlation between grain size, optical birefringence, and transparency is discussed for tetragonal zirconia (ZrO(2)) ceramics using the Mie, Rayleigh, and Rayleigh-Gans-Debye scattering models. Our results demonstrate that at the degree of mean birefringence in the range (0.03-0.04) expected for tetragonal ZrO(2), only the Mie theory provides reasonable results. At small particle size (< 50 nm) the more straightforward Rayleigh approximation correlates with the Mie model. A real in-line transmission of similar to 50% at visible light and 1 mm thickness is expected at a mean grain size < 40 nm and similar to 70% at a mean grain size < 20 nm. At an infrared (IR) wavelength of 5 um there should not be any scattering caused by birefringence for grainsizes < 200 nm. Our simulations were validated with experimental data for tetragonal ZrO(2) (3 mol% Y(2)O(3)) ceramics made from a powder with an initial particle size of similar to 10 nm by sintering in air and using hot-isostatic pressi

Název v anglickém jazyce

Transparent Tetragonal Yttria-Stabilized Zirconia Ceramic: Influence of Scattering Caused by Birefringence

Popis výsledku anglicky

The correlation between grain size, optical birefringence, and transparency is discussed for tetragonal zirconia (ZrO(2)) ceramics using the Mie, Rayleigh, and Rayleigh-Gans-Debye scattering models. Our results demonstrate that at the degree of mean birefringence in the range (0.03-0.04) expected for tetragonal ZrO(2), only the Mie theory provides reasonable results. At small particle size (< 50 nm) the more straightforward Rayleigh approximation correlates with the Mie model. A real in-line transmission of similar to 50% at visible light and 1 mm thickness is expected at a mean grain size < 40 nm and similar to 70% at a mean grain size < 20 nm. At an infrared (IR) wavelength of 5 um there should not be any scattering caused by birefringence for grainsizes < 200 nm. Our simulations were validated with experimental data for tetragonal ZrO(2) (3 mol% Y(2)O(3)) ceramics made from a powder with an initial particle size of similar to 10 nm by sintering in air and using hot-isostatic pressi

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the American Ceramic Society

ISSN

0002-7820

e-ISSN

—

Svazek periodika

94

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

9

Strana od-do

1850-1858

Kód UT WoS článku

000291393400039

EID výsledku v databázi Scopus

—