Solute Segregation at 46.8deg(111) Twist Grain Boundary of a Phosphorus Doped Fe-2.3%V Alloy

Kód výsledku v IS VaVaI

RIV/00216305:26210/12:PU95881 - isvavai.cz

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Solute Segregation at 46.8deg(111) Twist Grain Boundary of a Phosphorus Doped Fe-2.3%V Alloy

Popis výsledku v původním jazyce

The Auger electron spectroscopy study on chemistry of the 46.8deh(111) twist grain boundary of an Fe-2.3%V alloy showed an extended phosphorus enrichment at temperatures in range of 500 degC and 800 degC. Simultaneously, slight but nearly independent segregation of vanadium was also detected. The standard enthalpy and entropy of grain boundary segregation of phosphorus and vanadium were determined according to the Guttmann model of multicomponent interfacial segregation. Obtained data clearly show thatcoincidence boundary is special (i.e. low energy interface). The data also fit well with the predictive model of grain boundary segregation and confirm that phosphorus segregates interstitially at the grain boundary while vanadium substitutes iron atomsin the interface structure

Název v anglickém jazyce

Solute Segregation at 46.8deg(111) Twist Grain Boundary of a Phosphorus Doped Fe-2.3%V Alloy

Popis výsledku anglicky

The Auger electron spectroscopy study on chemistry of the 46.8deh(111) twist grain boundary of an Fe-2.3%V alloy showed an extended phosphorus enrichment at temperatures in range of 500 degC and 800 degC. Simultaneously, slight but nearly independent segregation of vanadium was also detected. The standard enthalpy and entropy of grain boundary segregation of phosphorus and vanadium were determined according to the Guttmann model of multicomponent interfacial segregation. Obtained data clearly show thatcoincidence boundary is special (i.e. low energy interface). The data also fit well with the predictive model of grain boundary segregation and confirm that phosphorus segregates interstitially at the grain boundary while vanadium substitutes iron atomsin the interface structure

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

GA106/08/0369: Nové přístupy k inženýrství hranic zrn

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface Science

ISSN

0039-6028

e-ISSN

—

Svazek periodika

606

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

258-262

Kód UT WoS článku

000300458600024

EID výsledku v databázi Scopus

—