Constraint effect on the slow crack growth in polyethylene

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU98846" target="_blank" >RIV/00216305:26210/12:PU98846 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/12:00385514

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Constraint effect on the slow crack growth in polyethylene

Popis výsledku v původním jazyce

From the practical point of view, most relevant damage of the HDPE structures is determined by slow crack growth. In this case plastic deformations are localized just around the crack front. Due to this fact linear elastic fracture mechanics can be usedfor description of the stress field around the crack tip. The constraint effect is mainly effect of the structure geometry and can be quantified by T-stress. Two different test specimens with different constraint level (T-stress) were prepared: single edge notched specimen and modified SEN specimen. The crack mouth opening displacement, crack tip opening displacement and crack length was measured. Than effect of the constraint and relation between CMOD and crack length was investigated and discussed.

Název v anglickém jazyce

Constraint effect on the slow crack growth in polyethylene

Popis výsledku anglicky

From the practical point of view, most relevant damage of the HDPE structures is determined by slow crack growth. In this case plastic deformations are localized just around the crack front. Due to this fact linear elastic fracture mechanics can be usedfor description of the stress field around the crack tip. The constraint effect is mainly effect of the structure geometry and can be quantified by T-stress. Two different test specimens with different constraint level (T-stress) were prepared: single edge notched specimen and modified SEN specimen. The crack mouth opening displacement, crack tip opening displacement and crack length was measured. Than effect of the constraint and relation between CMOD and crack length was investigated and discussed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Structural Integrity

ISSN

1757-9864

e-ISSN

—

Svazek periodika

3

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

118-126

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—