Prediction of the crack bifurcation in layered ceramics with high residual stresses

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F13%3APU104470" target="_blank" >RIV/00216305:26210/13:PU104470 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.engfracmech.2013.03.013" target="_blank" >http://dx.doi.org/10.1016/j.engfracmech.2013.03.013</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.engfracmech.2013.03.013" target="_blank" >10.1016/j.engfracmech.2013.03.013</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Prediction of the crack bifurcation in layered ceramics with high residual stresses

Popis výsledku v původním jazyce

A computational tool, aiming to predict the crack propagation (i.e. straight propagation, single deflection or bifurcation) in layered ceramics designed with internal residual stres- ses, is developed. The computational model is based on Finite FractureMechanics theory, especially focused on cracks terminating at the interface between two different material layers. The method utilises a matched asymptotic procedure to derive the change of potential energy associated with the fracture process. A combined loading (thermal and mechanical) is taken into consideration to clarify the influence of the residual stresses on the crack path during fracture.

Název v anglickém jazyce

Prediction of the crack bifurcation in layered ceramics with high residual stresses

Popis výsledku anglicky

A computational tool, aiming to predict the crack propagation (i.e. straight propagation, single deflection or bifurcation) in layered ceramics designed with internal residual stres- ses, is developed. The computational model is based on Finite FractureMechanics theory, especially focused on cracks terminating at the interface between two different material layers. The method utilises a matched asymptotic procedure to derive the change of potential energy associated with the fracture process. A combined loading (thermal and mechanical) is taken into consideration to clarify the influence of the residual stresses on the crack path during fracture.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.30.0005" target="_blank" >EE2.3.30.0005: Podpora tvorby excelentních týmů mezioborového výzkumu na VUT</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

—

Svazek periodika

2013

Číslo periodika v rámci svazku

108

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

19

Strana od-do

120-138

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—