Ductile damage identification and tensile notch effect for Eurofer97 steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F13%3APU104725" target="_blank" >RIV/00216305:26210/13:PU104725 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/13:00399630

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Ductile damage identification and tensile notch effect for Eurofer97 steel

Popis výsledku v původním jazyce

The effect of stress multiaxiality on void nucleation and growth at ductile fracture was studied for a Eurofer97 steel. Tensile testing of smooth and notched round bars was performed. The fractography and metallography analysis on broken halves of tensile bars together with the image analysis were carried out. The increasing stress multiaxiality in the bars lowers the strain at fracture. The ductile damage of the steel consists from the nucleation of the voids by decohesion mechanims, their gradual growth and finishes by rapid void coalescence. The increasing stress multiaxiality causes larger growth of voids together with observed restriction of void nucelation.

Název v anglickém jazyce

Ductile damage identification and tensile notch effect for Eurofer97 steel

Popis výsledku anglicky

The effect of stress multiaxiality on void nucleation and growth at ductile fracture was studied for a Eurofer97 steel. Tensile testing of smooth and notched round bars was performed. The fractography and metallography analysis on broken halves of tensile bars together with the image analysis were carried out. The increasing stress multiaxiality in the bars lowers the strain at fracture. The ductile damage of the steel consists from the nucleation of the voids by decohesion mechanims, their gradual growth and finishes by rapid void coalescence. The increasing stress multiaxiality causes larger growth of voids together with observed restriction of void nucelation.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta metalurgica slovaca

ISSN

1338-1660

e-ISSN

—

Svazek periodika

2013(3)

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

6

Strana od-do

185-190

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—