Crack Deflection from the Interface between Two Orthotropic Materials-Effect of Higher Order Terms in Asymptotic Analysis
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU104482" target="_blank" >RIV/00216305:26210/14:PU104482 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.577-578.157" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.577-578.157</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.577-578.157" target="_blank" >10.4028/www.scientific.net/KEM.577-578.157</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crack Deflection from the Interface between Two Orthotropic Materials-Effect of Higher Order Terms in Asymptotic Analysis
Popis výsledku v původním jazyce
The problem of crack deflection from the interface between two orthotropic materials is analyzed using the concept of Finite fracture mechanics and matched asymptotic procedure. A fracture criterion based on the energy approach is introduced for this problem. The main input for such criterion is the complex stress intensity factor calculated e.g. using the two-state integral. However for more precise predictions of the crack propagation also higher order terms of the asymptotic expansion are advisable to involve in the fracture criterion. To this end a T-stress term will be calculated and considered as the second input parameter. The matched asymptotic procedure together with FEM is used to derive the change of the potential energy induced by the incremental crack growth.
Název v anglickém jazyce
Crack Deflection from the Interface between Two Orthotropic Materials-Effect of Higher Order Terms in Asymptotic Analysis
Popis výsledku anglicky
The problem of crack deflection from the interface between two orthotropic materials is analyzed using the concept of Finite fracture mechanics and matched asymptotic procedure. A fracture criterion based on the energy approach is introduced for this problem. The main input for such criterion is the complex stress intensity factor calculated e.g. using the two-state integral. However for more precise predictions of the crack propagation also higher order terms of the asymptotic expansion are advisable to involve in the fracture criterion. To this end a T-stress term will be calculated and considered as the second input parameter. The matched asymptotic procedure together with FEM is used to derive the change of the potential energy induced by the incremental crack growth.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
<a href="/cs/project/EE2.3.30.0005" target="_blank" >EE2.3.30.0005: Podpora tvorby excelentních týmů mezioborového výzkumu na VUT</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advances in Fracture and Damage Mechanics XII
ISBN
978-3-03785-830-1
ISSN
1013-9826
e-ISSN
—
Počet stran výsledku
4
Strana od-do
157-160
Název nakladatele
Trans Tech Publications
Místo vydání
Švýcarsko
Místo konání akce
Beijing
Datum konání akce
16. 6. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000336693900040