Effect of thermal barrier coating on low cycle fatigue behavioir of cast Inconel 713LC at 900 oC
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU108707" target="_blank" >RIV/00216305:26210/14:PU108707 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.scientific.net/AMR.891-892.848" target="_blank" >http://www.scientific.net/AMR.891-892.848</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.891-892.848" target="_blank" >10.4028/www.scientific.net/AMR.891-892.848</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of thermal barrier coating on low cycle fatigue behavioir of cast Inconel 713LC at 900 oC
Popis výsledku v původním jazyce
Cast polycrystalline nickel base superalloy Inconel 713LC is used for critical parts of gas turbine engines that are subjected to repeated elastic-plastic loading in aggressive environments at variable temperatures. Thermal barrier coatings (TBC) can prolong the component life particularly by a reduction of temperature gradient during heating and cooling. In the present work, the high temperature low cycle fatigue behaviour of cast nickel-based superalloy Inconel 713LC in as-received condition and with TBC was studied. The microstructure of the material is characterized by dendritic grains with carbides and shrinkage pores. The average grain size was 0.66 mm.
Název v anglickém jazyce
Effect of thermal barrier coating on low cycle fatigue behavioir of cast Inconel 713LC at 900 oC
Popis výsledku anglicky
Cast polycrystalline nickel base superalloy Inconel 713LC is used for critical parts of gas turbine engines that are subjected to repeated elastic-plastic loading in aggressive environments at variable temperatures. Thermal barrier coatings (TBC) can prolong the component life particularly by a reduction of temperature gradient during heating and cooling. In the present work, the high temperature low cycle fatigue behaviour of cast nickel-based superalloy Inconel 713LC in as-received condition and with TBC was studied. The microstructure of the material is characterized by dendritic grains with carbides and shrinkage pores. The average grain size was 0.66 mm.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advanced Materials Research
ISBN
—
ISSN
1022-6680
e-ISSN
1662-8985
Počet stran výsledku
6
Strana od-do
848-853
Název nakladatele
Trans Tech Publications
Místo vydání
Switzerland
Místo konání akce
Praha
Datum konání akce
6. 6. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000337767700132