Influence of the T-stress on the crack bifurcation phenomenon in ceramic laminates

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU109676" target="_blank" >RIV/00216305:26210/14:PU109676 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.mspro.2014.06.173" target="_blank" >http://dx.doi.org/10.1016/j.mspro.2014.06.173</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.mspro.2014.06.173" target="_blank" >10.1016/j.mspro.2014.06.173</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of the T-stress on the crack bifurcation phenomenon in ceramic laminates

Popis výsledku v původním jazyce

The influence of the compressive residual stresses and layer thickness in ceramic laminates on the presence of the crack bifurcation phenomenon is numerically investigated in this contribution. Using the fracture criterion, based on the Finite Fracture Mechanics, the angle and type of crack propagation (single crack deflection/bifurcation) within the layers with large compressive stresses is investigated. Laminates with various thicknesses of the compressive layer and constant level of the compressive residual stresses are used for this purpose. In these cases, the level of the T-stress (in the vicinity of the crack tip) can play a role as a second parameter in the fracture criterion (next to the stress intensity factor) and as a consequence can this term influence the predicted crack propagation behaviour.

Název v anglickém jazyce

Influence of the T-stress on the crack bifurcation phenomenon in ceramic laminates

Popis výsledku anglicky

The influence of the compressive residual stresses and layer thickness in ceramic laminates on the presence of the crack bifurcation phenomenon is numerically investigated in this contribution. Using the fracture criterion, based on the Finite Fracture Mechanics, the angle and type of crack propagation (single crack deflection/bifurcation) within the layers with large compressive stresses is investigated. Laminates with various thicknesses of the compressive layer and constant level of the compressive residual stresses are used for this purpose. In these cases, the level of the T-stress (in the vicinity of the crack tip) can play a role as a second parameter in the fracture criterion (next to the stress intensity factor) and as a consequence can this term influence the predicted crack propagation behaviour.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

20th European Conference on Fracture (ECF 2014)

ISBN

9781632669094

ISSN

2211-8128

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1062-1067

Název nakladatele

Elsevier

Místo vydání

Trondheim, Norsko

Místo konání akce

Beijing

Datum konání akce

16. 6. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000398274600168