Decreasing thermal stresses in steam generator collector welds area using external cooling

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU110267" target="_blank" >RIV/00216305:26210/14:PU110267 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S2211812816000122" target="_blank" >http://www.sciencedirect.com/science/article/pii/S2211812816000122</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.mspro.2016.03.003" target="_blank" >10.1016/j.mspro.2016.03.003</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Decreasing thermal stresses in steam generator collector welds area using external cooling

Popis výsledku v původním jazyce

Presented paper deals with possibility of external cooling of steam generator welds area to decrease internal tensile thermal stresses which are one of the causes of cracking in this area. On various WWER-440 nuclear power plants (NPP) steam generators (SG) occurred quite serious problem of cracking in weld joints connecting primary collectors to the SG vessels nozzle. The cause of this cracking is stress corrosion cracking (SCC) mechanism. Results of these analyses showed that by proper external cooling of the weld area it is possible not just to decrease significantly existing tensile stresses, but to change them into compressive ones. This of course would have great impact on crack occurrence and growth.

Název v anglickém jazyce

Decreasing thermal stresses in steam generator collector welds area using external cooling

Popis výsledku anglicky

Presented paper deals with possibility of external cooling of steam generator welds area to decrease internal tensile thermal stresses which are one of the causes of cracking in this area. On various WWER-440 nuclear power plants (NPP) steam generators (SG) occurred quite serious problem of cracking in weld joints connecting primary collectors to the SG vessels nozzle. The cause of this cracking is stress corrosion cracking (SCC) mechanism. Results of these analyses showed that by proper external cooling of the weld area it is possible not just to decrease significantly existing tensile stresses, but to change them into compressive ones. This of course would have great impact on crack occurrence and growth.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20305 - Nuclear related engineering; (nuclear physics to be 1.3);

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Procedia Materials Science

ISBN

978-80-248-2802-2

ISSN

2211-8128

e-ISSN

—

Počet stran výsledku

6

Strana od-do

12-17

Název nakladatele

Elsevier

Místo vydání

neuveden

Místo konání akce

Ostrava

Datum konání akce

8. 8. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000386622900003