MICROSTRUCTURE OF Fe-Al BINARY COLD SPRAY THICK DEPOSIT AFTER ANNEALING

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU112475" target="_blank" >RIV/00216305:26210/14:PU112475 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

MICROSTRUCTURE OF Fe-Al BINARY COLD SPRAY THICK DEPOSIT AFTER ANNEALING

Popis výsledku v původním jazyce

Examined FeAl deposits were produced by low-pressure cold spray technique using heated air (300 °C, 1.5 MPa) as working gas. Although metal powders were mixed in ratio 60/40 at.% Fe/Al, the final chemical composition of the 8-10 mm thick deposits changedstrongly favouring aluminum (approximately 80 at.% Al). Samples consisting of the deposited material were annealed isothermally in argon protective atmosphere. All annealing processes ran at temperatures from 250 °C to 750 °C for two hours. The overallchange of material character during annealing was evaluated: changes in the character of fracture behavior, local micro hardness of the evolving phases and residual powder particles. Microstructure and chemistry of the newly formed phases was evaluated using analytical electron microscopy.

Název v anglickém jazyce

MICROSTRUCTURE OF Fe-Al BINARY COLD SPRAY THICK DEPOSIT AFTER ANNEALING

Popis výsledku anglicky

Examined FeAl deposits were produced by low-pressure cold spray technique using heated air (300 °C, 1.5 MPa) as working gas. Although metal powders were mixed in ratio 60/40 at.% Fe/Al, the final chemical composition of the 8-10 mm thick deposits changedstrongly favouring aluminum (approximately 80 at.% Al). Samples consisting of the deposited material were annealed isothermally in argon protective atmosphere. All annealing processes ran at temperatures from 250 °C to 750 °C for two hours. The overallchange of material character during annealing was evaluated: changes in the character of fracture behavior, local micro hardness of the evolving phases and residual powder particles. Microstructure and chemistry of the newly formed phases was evaluated using analytical electron microscopy.

Druh

D - Stať ve sborníku

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metal 2014

ISBN

978-80-87294-52-9

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1328-1333

Název nakladatele

Neuveden

Místo vydání

Neuveden

Místo konání akce

Brno

Datum konání akce

21. 5. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—