BIODEGRADATION PROPERTIES OF AZ31 MAGNESIUM ALLOY COATED BY DICALCIUM PHOSPHATE DIHYDRATE
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU113363" target="_blank" >RIV/00216305:26210/14:PU113363 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.uniza.sk/komunikacie/archiv/2014/3a/3a_2014en.pdf" target="_blank" >http://www.uniza.sk/komunikacie/archiv/2014/3a/3a_2014en.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
BIODEGRADATION PROPERTIES OF AZ31 MAGNESIUM ALLOY COATED BY DICALCIUM PHOSPHATE DIHYDRATE
Popis výsledku v původním jazyce
Biodegradation properties of magnesium and its alloys that can be used for implants are not satisfactory and cause serious problems. These problems can be solved by biodegradable surface coatings. Evaluation of biodegradation process of Mg-3Al-1Zn alloy surfaces after grinding and grinding followed by potential controlled electrodeposition of dicalcium phosphate dihydrate (DCPD) was investigated by electro-chemical impedance spectroscopy measurements in this study. The potentiostatic electrodeposition treatment process was performed in water solutionof Ca(NO3)2.4H2, NH4H2PO4and H2O2. The corrosion process on treated and nontreated samples after various exposure times wasevaluated in 0.9% NaCl solution simulating body fluid environment at 37 °C.
Název v anglickém jazyce
BIODEGRADATION PROPERTIES OF AZ31 MAGNESIUM ALLOY COATED BY DICALCIUM PHOSPHATE DIHYDRATE
Popis výsledku anglicky
Biodegradation properties of magnesium and its alloys that can be used for implants are not satisfactory and cause serious problems. These problems can be solved by biodegradable surface coatings. Evaluation of biodegradation process of Mg-3Al-1Zn alloy surfaces after grinding and grinding followed by potential controlled electrodeposition of dicalcium phosphate dihydrate (DCPD) was investigated by electro-chemical impedance spectroscopy measurements in this study. The potentiostatic electrodeposition treatment process was performed in water solutionof Ca(NO3)2.4H2, NH4H2PO4and H2O2. The corrosion process on treated and nontreated samples after various exposure times wasevaluated in 0.9% NaCl solution simulating body fluid environment at 37 °C.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
<a href="/cs/project/7AMB14SK080" target="_blank" >7AMB14SK080: Korozní degradace hořčíkových slitin a jejich interakce s biologickými systémy</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Communications
ISSN
1335-4205
e-ISSN
—
Svazek periodika
16
Číslo periodika v rámci svazku
3A
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
5
Strana od-do
189-193
Kód UT WoS článku
—
EID výsledku v databázi Scopus
2-s2.0-84920008383