Influence of the beam deflection od properties of the electron beam hardened layer

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F17%3APU124730" target="_blank" >RIV/00216305:26210/17:PU124730 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of the beam deflection od properties of the electron beam hardened layer

Popis výsledku v původním jazyce

The usage of the high-energetic source of the electron beam enables a repeated surface quenching of the chosen areas of an engineering part surface. Different techniques of the electron beam deflections allow the creation of hardened layers of different shapes and above all the thicknesses. The deflection was tested at one point, six points, a line and a field on the material 42CrMo4 (1.7225). The effect of the process speed and defocusing of the electron beam was studied. The electron beam surface quenching resulted in a very fine martensitic microstructure with the hardness over 700 HV0.5. The thickness of the hardened layers depends on the type of deflection and depends directly on the process speed. The maximum observed depth was 1.49 mm. The electron beam defocusing affects the width of the hardened track and can cause an extension of the trace up to 40%. The hardness values continuously decrease from the surface to the material volume.

Název v anglickém jazyce

Influence of the beam deflection od properties of the electron beam hardened layer

Popis výsledku anglicky

The usage of the high-energetic source of the electron beam enables a repeated surface quenching of the chosen areas of an engineering part surface. Different techniques of the electron beam deflections allow the creation of hardened layers of different shapes and above all the thicknesses. The deflection was tested at one point, six points, a line and a field on the material 42CrMo4 (1.7225). The effect of the process speed and defocusing of the electron beam was studied. The electron beam surface quenching resulted in a very fine martensitic microstructure with the hardness over 700 HV0.5. The thickness of the hardened layers depends on the type of deflection and depends directly on the process speed. The maximum observed depth was 1.49 mm. The electron beam defocusing affects the width of the hardened track and can cause an extension of the trace up to 40%. The hardness values continuously decrease from the surface to the material volume.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/LO1202" target="_blank" >LO1202: NETME CENTRE PLUS</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

International Scientific Journal "Material Science" "Nonequilibrium Phase Transformations"

ISBN

—

ISSN

2367-749X

e-ISSN

—

Počet stran výsledku

4

Strana od-do

194-197

Název nakladatele

Neuveden

Místo vydání

Neuveden

Místo konání akce

Varna

Datum konání akce

11. 9. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—