INLUENCE OF LOADING CYCLE ASYMMETRY AND LONG-TERM THERMAL EXPOSURE ON FATIGUE CRACK GROWTH RATE IN MARTENSITIC P91 AND P92 STEELS

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F21%3APU147606" target="_blank" >RIV/00216305:26210/21:PU147606 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/25870807:_____/21:N0000002
Výsledek na webu
<a href="https://www.scopus.com/record/display.uri?eid=2-s2.0-85124348502&origin=inward&txGid=4f84e9b60a1c7afa72de0d2faaa6bfc9" target="_blank" >https://www.scopus.com/record/display.uri?eid=2-s2.0-85124348502&origin=inward&txGid=4f84e9b60a1c7afa72de0d2faaa6bfc9</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.37904/metal.2021.4127" target="_blank" >10.37904/metal.2021.4127</a>

Jazyk výsledku
angličtina
Název v původním jazyce
INLUENCE OF LOADING CYCLE ASYMMETRY AND LONG-TERM THERMAL EXPOSURE ON FATIGUE CRACK GROWTH RATE IN MARTENSITIC P91 AND P92 STEELS
Popis výsledku v původním jazyce
The paper deals with the effect of different loading cycle asymmetry and long-term thermal exposure on fatigue crack growth rate in P91 and P92 steels used primarily for components in USC powerplants. Testing was performed using C(T) specimens. Fatigue crack growth was measured in II. stage of crack growth described by Paris law from both sides using optical microscope. Loading cycle asymmetry effect was assessed for each steel grade before the thermal exposure and then compared with state after the long-term thermal exposure.
Název v anglickém jazyce
INLUENCE OF LOADING CYCLE ASYMMETRY AND LONG-TERM THERMAL EXPOSURE ON FATIGUE CRACK GROWTH RATE IN MARTENSITIC P91 AND P92 STEELS
Popis výsledku anglicky
The paper deals with the effect of different loading cycle asymmetry and long-term thermal exposure on fatigue crack growth rate in P91 and P92 steels used primarily for components in USC powerplants. Testing was performed using C(T) specimens. Fatigue crack growth was measured in II. stage of crack growth described by Paris law from both sides using optical microscope. Loading cycle asymmetry effect was assessed for each steel grade before the thermal exposure and then compared with state after the long-term thermal exposure.

Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku
Proceedings 30th Anniversary International Conference on Metallurgy and Materials
ISBN
978-80-87294-99-4
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
366-371
Název nakladatele
MDPI
Místo vydání
neuveden
Místo konání akce
Brno
Datum konání akce
26. 5. 2021
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—

Podobné výsledky(10)