Prediction of the fatigue life of notched specimens: The influence of the surface quality produced by machining

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F23%3APU147138" target="_blank" >RIV/00216305:26210/23:PU147138 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S2452321622008186" target="_blank" >https://www.sciencedirect.com/science/article/pii/S2452321622008186</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.prostr.2022.12.255" target="_blank" >10.1016/j.prostr.2022.12.255</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Prediction of the fatigue life of notched specimens: The influence of the surface quality produced by machining

Popis výsledku v původním jazyce

The article introduces a method for fatigue lifetime predictions of notched specimens. The method uses fracture stresses of smooth and notched specimens with notch radius r = 0.2 mm. These two sets of experimental data are evaluated with the knowledge of axial stress distributions of the notched specimens using average stress over a length parameter l. This parameter l is considered to be a material characteristic (depending on the number of cycles to failure) and can be used for lifetime predictions of notched specimens with various notch radii. The predictions are compared to experimental data and analyzed. There is a strong influence of the process of machining of notches, which can lead to fatigue failure earlier than predicted. The data are evaluated in the area of high cycle fatigue and gigacycle fatigue.

Název v anglickém jazyce

Prediction of the fatigue life of notched specimens: The influence of the surface quality produced by machining

Popis výsledku anglicky

The article introduces a method for fatigue lifetime predictions of notched specimens. The method uses fracture stresses of smooth and notched specimens with notch radius r = 0.2 mm. These two sets of experimental data are evaluated with the knowledge of axial stress distributions of the notched specimens using average stress over a length parameter l. This parameter l is considered to be a material characteristic (depending on the number of cycles to failure) and can be used for lifetime predictions of notched specimens with various notch radii. The predictions are compared to experimental data and analyzed. There is a strong influence of the process of machining of notches, which can lead to fatigue failure earlier than predicted. The data are evaluated in the area of high cycle fatigue and gigacycle fatigue.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure & Micromechanics of Fracture

ISBN

—

ISSN

2452-3216

e-ISSN

—

Počet stran výsledku

6

Strana od-do

178-183

Název nakladatele

Elsevier

Místo vydání

neuveden

Místo konání akce

Brno

Datum konání akce

12. 9. 2022

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—