Fatigue behavior of DIN 1.4307 and DIN 1.4306 stainless steels under high frequency loading

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F23%3APU147150" target="_blank" >RIV/00216305:26210/23:PU147150 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S2452321622008125" target="_blank" >https://www.sciencedirect.com/science/article/pii/S2452321622008125</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.prostr.2022.12.249" target="_blank" >10.1016/j.prostr.2022.12.249</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue behavior of DIN 1.4307 and DIN 1.4306 stainless steels under high frequency loading

Popis výsledku v původním jazyce

Two stainless steels DIN 1.4307 and DIN 1.4306 were tested by an ultrasonic fatigue loading device under push-pull mode (stress ratio R = -1). Life-time curves were determined in the high and very high cycle fatigue regions. The time dependence of frequency was monitored and evaluated. At the beginning of the tests (up to 1 × 107 cycles), an increase of the frequency was observed, followed by a slow frequency decrease. It relates to changes of microstructure. No failure occurred in the region between 1 × 109 and 1 × 1010 cycles. The steel 1.4306 exhibits a higher fatigue life-time than the steel 1.4307. This is caused by the difference in the chemical composition of the two steels, namely by the higher nickel content in the 1.4306 steel.

Název v anglickém jazyce

Fatigue behavior of DIN 1.4307 and DIN 1.4306 stainless steels under high frequency loading

Popis výsledku anglicky

Two stainless steels DIN 1.4307 and DIN 1.4306 were tested by an ultrasonic fatigue loading device under push-pull mode (stress ratio R = -1). Life-time curves were determined in the high and very high cycle fatigue regions. The time dependence of frequency was monitored and evaluated. At the beginning of the tests (up to 1 × 107 cycles), an increase of the frequency was observed, followed by a slow frequency decrease. It relates to changes of microstructure. No failure occurred in the region between 1 × 109 and 1 × 1010 cycles. The steel 1.4306 exhibits a higher fatigue life-time than the steel 1.4307. This is caused by the difference in the chemical composition of the two steels, namely by the higher nickel content in the 1.4306 steel.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA20-00761S" target="_blank" >GA20-00761S: Vliv materiálových vlastností korozivzdorných ocelí na spolehlivost mostních konstrukcí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure & Micromechanics of Fracture

ISBN

—

ISSN

2452-3216

e-ISSN

—

Počet stran výsledku

6

Strana od-do

142-147

Název nakladatele

Elsevier

Místo vydání

neuveden

Místo konání akce

Brno

Datum konání akce

12. 9. 2022

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—