Preparation and Properties of SnO2 and V2O5 Thin Layers for Electrochromic Device

Popis výsledku v původním jazyce

The tin oxide thin films doped with the fluorine and the antimony were prepared by a spray pyrolysis method from SnCl2 precursor. The respective deposition temperature was 420°C. The fluorine and antimony dopant ratio were varied and the lowest resistivity was founded for the both type of dopants. The films have moderate an optical transmission. The vanadium oxide films were dip-coated on the FTO (0,7 wt. %) layers. The coating solution was prepared by dissolving a V2O5 powder in a H2O2 solution. The coovered FTO layers were annealed at 150°C for 1 hour. The 0,5M LiClO4/PC gel electrolyte was used as a ion conductor layer. The vanadium oxide films showed a reversible multichromism (yellow green blue) upon Li+ ion insertion/extraction. The transmittancemodulation range can be varied by adjusting the film thickness. The vanadium oxide films with a proper thickness could be used in a realization of multicolored electrochromic devices.

Název v anglickém jazyce

Preparation and Properties of SnO2 and V2O5 Thin Layers for Electrochromic Device

Popis výsledku anglicky

The tin oxide thin films doped with the fluorine and the antimony were prepared by a spray pyrolysis method from SnCl2 precursor. The respective deposition temperature was 420°C. The fluorine and antimony dopant ratio were varied and the lowest resistivity was founded for the both type of dopants. The films have moderate an optical transmission. The vanadium oxide films were dip-coated on the FTO (0,7 wt. %) layers. The coating solution was prepared by dissolving a V2O5 powder in a H2O2 solution. The coovered FTO layers were annealed at 150°C for 1 hour. The 0,5M LiClO4/PC gel electrolyte was used as a ion conductor layer. The vanadium oxide films showed a reversible multichromism (yellow green blue) upon Li+ ion insertion/extraction. The transmittancemodulation range can be varied by adjusting the film thickness. The vanadium oxide films with a proper thickness could be used in a realization of multicolored electrochromic devices.

Druh

D - Stať ve sborníku

CEP obor

CG - Elektrochemie

OECD FORD obor

—

Projekt

<a href="/cs/project/KJB208130604" target="_blank" >KJB208130604: Výzkum pohyblivosti a vodivosti iontů v gelových elektrolytech metodou nukleární magnetické rezonance</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the 12th Conference Student EEICT 2006

ISBN

80-214-3162-8

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

206-210

Název nakladatele

VUT v Brně

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

27. 4. 2006

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—