Cobalt Doped LiFePO4/C Composite Material for Li-Ion Cathodes
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F12%3APU98862" target="_blank" >RIV/00216305:26220/12:PU98862 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Cobalt Doped LiFePO4/C Composite Material for Li-Ion Cathodes
Popis výsledku v původním jazyce
High temperature solid state synthesis was used for preparation of LiFePO4/C composite material and cobalt doped LiFePO4/C composite material. Glycine assisted combustion method was involved as a carbon coating procedure. It uses glycine as a carbon precursor for conductive coating and connecting of active material nanoparticles. Two different samples were prepared and investigated - clear LiFePO4/C material and LiFePO4/C doped with 1% of cobalt. The aim of this work is to show how a supervalent ion of cobalt influences parameters of cathode material. Electrochemical characterization by galvanostatic cycling, electrochemical impedance spectroscopy and rate capability was made and physical characterization by SEM, TEM and X-ray diffraction was provided.
Název v anglickém jazyce
Cobalt Doped LiFePO4/C Composite Material for Li-Ion Cathodes
Popis výsledku anglicky
High temperature solid state synthesis was used for preparation of LiFePO4/C composite material and cobalt doped LiFePO4/C composite material. Glycine assisted combustion method was involved as a carbon coating procedure. It uses glycine as a carbon precursor for conductive coating and connecting of active material nanoparticles. Two different samples were prepared and investigated - clear LiFePO4/C material and LiFePO4/C doped with 1% of cobalt. The aim of this work is to show how a supervalent ion of cobalt influences parameters of cathode material. Electrochemical characterization by galvanostatic cycling, electrochemical impedance spectroscopy and rate capability was made and physical characterization by SEM, TEM and X-ray diffraction was provided.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CG - Elektrochemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
ECS Transaction
ISSN
1938-6737
e-ISSN
—
Svazek periodika
40
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
5
Strana od-do
93-97
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—